A bath T/C spandex fabric scales agent dye structure and dyeing process and one bath dyeing agent structure according to the weight percentage of XF/R ETT 1%, including the brilliant blue turquoise blue 0.8%, blue 0.3%, 2BLN 3RL 0.6%, FBL brilliant blue turquoise blue 0.45%, blue 0.1%, acid D/RGL blended polyester dyeing one bath agent 1.5%, 3% hydrogen peroxide 0.5%, dispersant, mixed with one bath deoiling agent 0.5%, spandex oil removal agent 0.5% and 1:40 sodium sulfate dilution 18%, water 73.05%, fabric dyed: 1:10; dyeing process including dyeing and washing, dyeing process including temperature, substrate into the cylinder, heating, cooling, washing cloth out of the cylinder; the process includes 1, rinsing dyed fabric, 2, cloth into the solution containing 0.5% formaldehyde free fixing agent in 80 ~ C insulation 15min.
【技术实现步骤摘要】
一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺
本专利技术涉及一种漂染工艺，特别涉及一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺，漂染工程
技术介绍
传统工艺的涤棉氨纶布的漂染工艺中，在染色前一般都要进行独立工艺的前处理和氧漂后才能进行染色。在这个前处理和氧漂工艺过程中，不但需要消耗大量的助剂、人工、工艺周期，同时还要消耗大量的水资源和电能，这不但给企业增加了很大一部分的工艺成本，同时还要消耗大量的宝贵资源，与节能高效的现代企业理念大相径庭。
技术实现思路
为了解决上述涤棉氨纶染色前需要单独进行前处理的技术缺陷，本专利技术提供一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺。本专利技术所采用的技术方案是：一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺，一浴剂染液结构按重量百分比包括XF/R艳蓝1.0%、ETT翠蓝0.8%、2BLN蓝0.3%、3RL艳蓝0.6%、FBL翠蓝0.45%、D/RGL混纺蓝0.1%、酸性涤棉漂染一浴剂1.5%、双氧水3%、分散剂0.5%、混染同浴去油剂0.5%、氨纶除油剂0.5%、1:40的元明粉稀释液18%、水73.05%，基布：...
【技术保护点】
一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺，其特征是：一浴剂染液结构按重量百分比包括XF/R艳蓝1.0%、ETT翠蓝0.8%、2BLN蓝0.3%、3RL艳蓝0.6%、FBL翠蓝0.45%、D/RGL混纺蓝0.1%、酸性涤棉漂染一浴剂1.5%、双氧水3%、分散剂0.5%、混染同浴去油剂0.5%、氨纶除油剂0.5%、1:40的元明粉稀释液18%、水73.05%，基布：染为1:10；漂染工艺包括染色工艺和漂洗工艺，染色工艺包括将染液升温到80°C、基布入缸、按2.5°C/ min将染液升温到130°C、保温30 min、按2.5°C/ min将染液降温到80°C然后基布出缸；...
【技术特征摘要】
1.一种T/C氨纶鱼鳞布的一浴剂染液结构和漂染工艺，其特征是：一浴剂染液结构按重量百分比包括XF/R艳蓝1.0%、ETT翠蓝0.8%、2BLN蓝0.3%、3RL艳蓝0.6%、FBL翠蓝0.45%、D/RGL混纺蓝0.1%、酸性涤棉漂染一浴剂1.5%、双氧水3%、分散剂0.5%、混染同浴去油剂0.5%、氨纶除油剂0.5%、1:40的元明粉稀...