A gray cast iron casting flow with excellent performance, which belongs to the technical field of powder metallurgy, C by 4.2% ~ 6.77%, 2.5% ~ 3.8% Mn, Si 1.05% ~ 1.55%, 0.05 ~ 0.128% S, P 0.125% ~ 0.625%, 0.45% ~ 0.85% Cu, Cr 0.62% ~ 0.98%, 0.07 ~ 0.12% Sn Sb,, Ni 0.77%, W 0.02% 1.2%, margin for Fe. The new composition is novel, the production process is reasonable and clear, and the smelting process is easy to control. The gray iron produced by this process has superior casting performance, so as to solve the problem of large shrinkage porosity of gray iron products. The production method of grey cast iron has the advantages of no shrinkage cavity and high yield, and it can meet the material requirements of high performance and heavy castings at present.
【技术实现步骤摘要】
一种铸造流动性能优异的灰铸铁
本专利技术属于粉末冶金
，涉及一种灰铸铁，特别是涉及一种铸造流动性能优异的灰铸铁。
技术介绍
铸铁主要由铁、碳和硅组成的合金的总称。铸铁可分为：灰口铸铁、白口铸铁、可锻铸铁、球磨铸铁、蠕墨铸铁以及合金铸铁。合金铸铁是在普通铸铁加入适量合金元素（如硅、锰、磷、镍、铬、钼、铜、铝、硼、钒、锡等）获得。合金元素使铸铁的基体组织发生变化，从而具有相应的耐热、耐磨、耐蚀、耐低温或无磁等特性。其中，合金铸铁中的灰铸铁由于成本低廉，并具有铸造性、可加工性的特点，是工业中应用最广泛的一种铸铁，如广泛用于制造如发动机、家电的零部件等。现有的灰铸铁的组成是由其所制造的部件性能要求如拉伸强度、磨损性能、机械加工性等来决定的，目前通常采用折衷的方式来进行配比选择，因此现有的灰铸铁的组成范围相当宽。但是，当灰铸铁用于制作对耐磨性要求较高的部件时，很难达到耐磨性的要求。因此，提供一种提高耐磨性以作为现有性能的补充的高硬度、高耐磨的合金铸铁成为了业界需要解决的技术问题。
技术实现思路
本专利技术针对本专利技术为了解决传统灰铸铁件在铸造过程中流动性能差、耐磨性能低...
【技术保护点】
一种铸造流动性能优异的灰铸铁，其特征在于：由如下质量百分比的原料组成，C 4.2%～6.77%、Si 2.5%～3.8%、Mn 1.05%～1.55% 、P 0.05～0.128 %、S 0.125%～0.625%、Cr 0.45%～0.85%、Cu 0.62%～0.98%、Sn 0.07～0.12%、Sb 0.02%、Ni 0.77%、W 1.2%，余量为Fe。
【技术特征摘要】
1.一种铸造流动性能优异的灰铸铁，其特征在于：由如下质量百分比的原料组成，C4.2%～6.77%、Si2.5%～3.8%、Mn1.05%～1.55%、P0.05～0.128%、S0.125%～0.625%、Cr0.45%～0.85%、Cu0.62%～0.98%、Sn0.07～0.12%、Sb0.02%、Ni0.77%、W1.2%，余量为Fe。2.如权利要求1所述的一种铸造流动性能优异的灰铸铁的制造方法，其特征在于，步骤如下：(1)按品位等级的高低依次将生铁、废钢材和回炉料加入电炉内；(2)加热升温至1200度时加入Mn铁，并继续升温至1500-1550度生成熔融态的铁水；(3)保温并进行铁水除渣；(4)降温...