White cast iron and heat treatment process with fracture resistance, which belongs to the field of iron carbon alloy technology, chemical components by mass percentage is as follows: C 2 ~ 2.8%, 0.6 ~ 0.9% Cr, Si 6 ~ 7%, 0.2 ~ 0.38% Ni, Mn 3.6 ~ 4.2%, Mo = 0.98% P = 0.045%,, S = 0.06%, Fe margin. The invention has the advantages of novel component, the production process is reasonable and clear, through two times of quenching and tempering, quenching and tempering temperature are determined by experiments, were treated at this temperature, greatly improve the toughness and wear resistance of Ni hard white cast iron, the iron is not easy to crack during use, improve service life of casting state after heat treatment the hardness reaches 53HRC, processing time and greatly reduces the heat treatment, improve production efficiency.
【技术实现步骤摘要】
具有抗断裂性能的白口铸铁及热处理工艺
本专利技术属于铁碳合金
，涉及一种白口铸铁，特别是涉及一种具有抗断裂性能的白口铸铁及热处理工艺。
技术介绍
碳以渗碳体形态存在的铸铁，其断面为灰白色。是一种良好抗磨材料，在磨料磨损条件下工作。白口铸铁包括普通白口铸铁、低合金白口铸铁、中合金白口铸铁，高合金白口铸铁。普通白口铸铁中国早在春秋时代就制成了抗磨性良好的白口铸铁，用作一些抗磨零件。这种铸铁具有高碳低硅的特点，有较高的硬度，但很脆，适用于制造冲击载荷小的零件，一般用在犁铧、磨片、导板等方面。生产中常采用热处理的方法来改善其性能，扩大它的应用范围。碳对于普通白口铸铁的耐磨性能起最重要的作用，含碳量愈高，则形成的渗碳体愈多，构成大量的莱氏体，因而硬度愈高，耐磨性也就愈好。但含碳量高，韧性则下降。
技术实现思路
本专利技术针对普通白口铸铁在使用过程中出现韧性低、抗冲击性小、抗断裂性差等不足，提出具有抗断裂性能的白口铸铁及热处理工艺，其白口铸铁的组分更为合理、工作寿命更长，制造更为容易，能大大提升白口铸铁的力学性能，能满足强冲击等使用需求。本专利技术的技术方案是：具有抗断裂性...
【技术保护点】
具有抗断裂性能的白口铸铁，其特征在于：所述白口铸铁按质量百分含量计的化学成分如下：C 2.0～2.8％、Si 0.6～0.9％、Cr 6.0～7.0％、Mn 0.2～0.38％、Ni 3.6～4.2％、Mo ≤0.98％、P ≤ 0.045％、S ≤ 0.06％、Fe 余量。
【技术特征摘要】
1.具有抗断裂性能的白口铸铁，其特征在于：所述白口铸铁按质量百分含量计的化学成分如下：C2.0～2.8％、Si0.6～0.9％、Cr6.0～7.0％、Mn0.2～0.38％、Ni3.6～4.2％、Mo≤0.98％、P≤0.045％、S≤0.06％、Fe余量。2.如权利要求1所述的具有抗断裂性能的白口铸铁的热处理工艺，其特征在于，包括以下步骤：(1)淬火：将所述镍硬白口铸铁...