The invention discloses a high temperature resistant silicone coating, which consists of the following raw materials by weight: silicone resin: 30 40; 10: 5 heat resistant pigments; solvent: 20 30; 2 additives: 5; a method for producing silicone heat resistant coating and production method of the resistant silicone high temperature coating comprises the following steps: S1; atmospheric mixing; grinding; S2: S3 package. Silicone high temperature paint is made up of organosilicon, heat-resistant pigments, additives, solvents and so on. The products have quick drying, good adhesion, good flexibility, (single) two component packaging and convenient construction. The characteristics of high temperature resistant and non sticky coatings.
【技术实现步骤摘要】
一种有机硅耐高温涂料及其生产方法
本专利技术涉及有机硅耐高温涂料
，具体为一种有机硅耐高温涂料及其生产方法。
技术介绍
有机硅耐高温涂料是一种高性能的耐高温涂料，成膜后涂膜有良好的封闭性性能。该产品能(视色泽)耐250—800℃高温。适用于一切耐高温的环境，使其免受高温腐蚀介质的侵蚀。如发动机外壳、烟囱、排气管、热交换器等。产品具有表干燥迅速，附着力好、柔韧性好，(单)双组分包装、施工方便。耐高温等不粘涂料的特点。
技术实现思路
本专利技术的目的是为了解决现有技术中存在的缺点，而提出的一种有机硅耐高温涂料及其生产方法。为实现上述目的，本专利技术提供如下技术方案：一种有机硅耐高温涂料，由以下原料按照重量份组成：有机硅树脂：30份；耐热颜料：5份；溶剂：20份；助剂：2份；优选的，所述有机硅树脂。优选的，所述耐热颜料粒径为400目。优选的，一种有机硅耐高温涂料的生产方法，其特征在于：该有机硅耐高温涂料的生产方法包括以下步骤：S1：常压下搅拌：有机硅树脂：30份；耐热颜料：5份；溶剂：20份；助剂：2份；搅拌三十分钟到五十分钟,S2：进研磨机研磨至细度30umS3：包...
【技术保护点】
一种有机硅耐高温涂料，其特征在于：由以下原料按照重量份组成：有机硅树脂：30‑40份；耐热颜料：5‑10份；溶剂：20‑30份；助剂：2‑5份。
【技术特征摘要】
1.一种有机硅耐高温涂料，其特征在于：由以下原料按照重量份组成：有机硅树脂：30-40份；耐热颜料：5-10份；溶剂：20-30份；助剂：2-5份。2.根据权利要求1所述的一种有机硅耐高温涂料，其特征在于：由以下原料按照重量份组成：有机硅树脂：30份；耐热颜料：5份；溶剂：20份；助剂：2份。3.根据权利要求1所述的一种有机硅耐高温涂料，其特征在于：所述有机硅树脂。4.根据权利要求1所述的一种有机硅耐高温涂料，...
【专利技术属性】
技术研发人员：杨松林，
申请(专利权)人：江苏欣安新材料技术有限公司，
类型：发明
国别省市：江苏,32