The invention discloses a method, a bentonite which consists of the following steps: 1, 55 65 weight eighteen sixteen, 10 15 tertiary ammonium weight pure wine hardcover into a reaction kettle reactor, built in 20 degrees Celsius, stirring for 1.5 hours; while stirring slowly add 25 weight 30 the liquid chlorine and potassium alkyl; after mixing at a temperature of 20 60 degrees Celsius heat for 60 minutes, prepared eighteen alkyl ammonium chloride; step 2, 50 parts by weight of bentonite and stirring for 40 minutes to add water dilute suspensions, stirring slowly adding 2 weight portions of the prepared eighteen alkyl ammonium chloride, after mixing at a temperature of 20 60 degrees Celsius heat for 60 minutes, preparation of organic bentonite. The invention can make the organic bentonite clay is increased, viscosity enhancement, burning increased.
【技术实现步骤摘要】
一种膨润土的制作方法
本专利技术涉及一种轻工与化工领域，特别是涉及一种膨润土的制作方法。
技术介绍
有机膨润土是一种无机矿物/有机铵复合物，以膨润土为原料，利用膨润土中蒙脱石的层片状结构及其能在水或有机溶剂中溶胀分散成胶体级粘粒特性，通过离子交换技术插入有机覆盖剂而制成的。有机膨润土在各类有机溶剂、油类、液体树脂中能形成凝胶，具有良好的增稠性、触变性、悬浮稳定性、高温稳定性、润滑性、成膜性，耐水性及化学稳定性，在涂料工业中有重要的应用价值，在油漆油墨、航空、冶金、化纤、石油等工业中也有广泛的应用。但现有的方法生产出的有机膨润土粘度较差，白度不够并且灼烧量差。
技术实现思路
本专利技术所要解决的技术问题是提供一种膨润土的制作方法，能使生产出的有机膨润土白度增加、粘度增强、灼烧量提高。为解决上述技术问题，本专利技术提供的一种膨润土的制作方法，包括：步骤1、取55-65重量份十八十六叔铵、10-15重量份纯酒精装进反应釜，反应釜中内置20摄氏度，开动搅拌1.5小时；边搅拌边缓慢加入25-30重量份的液态氯钾烷；搅拌结束后在温度20-60摄氏度的环境中保温60分钟，制得十八烷...
【技术保护点】
一种膨润土的制作方法，其特征在于，包括：步骤1、取55‑65重量份十八十六叔铵、10‑15重量份纯酒精装进反应釜，反应釜中内置20摄氏度，开动搅拌1.5小时；边搅拌边缓慢加入25‑30重量份的液态氯钾烷；搅拌结束后在温度20‑60摄氏度的环境中保温60分钟，制得十八烷基氯化铵；步骤2、取50重量份的膨润土加水稀释至悬浮液并开动搅拌40分钟，边搅拌边缓慢加入2重量份所制得的十八烷基氯化铵，搅拌结束后在温度20‑60摄氏度的环境中保温60分钟，制得有机膨润土。
【技术特征摘要】
1.一种膨润土的制作方法，其特征在于，包括：步骤1、取55-65重量份十八十六叔铵、10-15重量份纯酒精装进反应釜，反应釜中内置20摄氏度，开动搅拌1.5小时；边搅拌边缓慢加入25-30重量份的液态氯钾烷；搅拌结束后在温度20-60摄氏度的环境中保温60分钟，制得十八烷基氯化铵；步骤2、取50重量份的膨润土加水稀释至悬浮液并开动搅拌40分钟，边搅拌边缓慢加入2重量份...
【专利技术属性】
技术研发人员：王李广，
申请(专利权)人：天津金戈科技发展有限责任公司，
类型：发明
国别省市：天津,12