The embodiment of the invention discloses a sodium bentonite and a preparation method thereof, relating to the technical field of sodium treatment. The sodium bentonite by weight of raw materials under the prepared calcium base bentonite 90 sodium 1 98 copies, 10 copies, 3 copies of the 1 tackifier, synergist of 0.5 2 copies, 1 copies of lubricants 0.01. The invention adopts the preparation method of acidification and recombination to avoid the chemical reaction between sulfuric acid and other components, meanwhile, the absorbability, stability and lubricity of the acidified bentonite are greatly improved. The preparation of the sodium bentonite has good thixotropy and lubricity, thermal stability, high plasticity, good adhesion, wet tensile strength and high dry strength characteristics, can meet the demand of various types of production.
【技术实现步骤摘要】
一种钠化膨润土及其制备方法
本专利技术涉及钠化处理
，尤其涉及一种钠化膨润土及其制备方法。
技术介绍
膨润土是粘土的一种，它的主要成分为蒙脱土，属于层状结构的含水硅铝酸盐矿物。由于它本身具有阳离子可交换特征，因此可以按所需用途制成不同系列的有机膨润土。有机膨润土常被作润滑剂的稠化剂、涂料的助剂、油漆的防沉降剂和增稠剂、石油钻井的解卡剂等。我国的膨润土资源极为丰富，大部分膨润土矿以钙基膨润土为主，而且品位低的钙基膨润土占多数；钠基膨润土的储藏量较少，但是钠基膨润土比钙基膨润土的性能要好，因此，为了提高钙基膨润土的性能，需要对钙基膨润土进行钠化改性处理。常规进行钙基膨润土钠化改性处理的方法，是将碳酸钠直接加入钙基膨润土原矿中，钠化后烘干和磨粉。目前，主要采用人工钠基工艺将钙基膨润土改性为钠基膨润土。钠基剂可以是碳酸钠、氟化钠和硫酸钠等，但从经济上考虑，碳酸钠是最好的钠基剂。钠基过程中，膨润土与碳酸钠发生反应形成的碳酸钙不溶于水，促进了反应向右进行，形成了钠基膨润土，但是，由于钙离子电势较强，膨润土有优先吸附钙离子能力，因此，上面的反应是可逆的，不可能达到100％...
【技术保护点】
一种钠化膨润土，其特征在于，包括以下的重量份数的原料制备而成：钙基膨润土90‑98份，钠盐1‑10份，增粘剂1‑3份，增效剂0.5‑2份，润滑剂0.01‑1份。
【技术特征摘要】
1.一种钠化膨润土，其特征在于，包括以下的重量份数的原料制备而成：钙基膨润土90-98份，钠盐1-10份，增粘剂1-3份，增效剂0.5-2份，润滑剂0.01-1份。2.根据权利要求1所述的一种钠化膨润土，其特征在于，包括以下重量份数的原料制备而成：钙基膨润土93-95份，钠盐3-8份，增粘剂1.5-2份，增效剂0.8-1份，润滑剂0.03-0.1份。3.根据权利要求1所述的一种钠化膨润土，其特征在于，所述钠盐是碳酸钠，硅酸钠，氟化钠，草酸钠，醋酸钠，磷酸类钠盐，聚丙烯酸钠，氢氧化钠，氯化钠，硫代硫酸钠，纤维素钠中的一种或多种混合物。4.根据权利要求1所述的一种钠化膨润土，其特征在于，所述增粘剂是氧化镁，氢氧化镁中的一种。5.根据权利要求1所述的一种钠化膨润土，其特征在于，所述增效剂是聚丙烯酰胺，丙烯酰胺中的一种。6.根据权利要求1所述的一种钠化膨润土，其特...
【专利技术属性】
技术研发人员：刘新兵，刘长淼，刘玉林，
申请(专利权)人：句容康泰膨润土有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。