The invention relates to a sodium bentonite preparation method, the method includes the following steps: 1) bentonite into a reactor with heating temperature control, mixing kneading function, slowly adding bentonite quality 1 10 times of water, stirring and kneading, heating up to 50 DEG C 80; 2 adding bentonite) surface quality of 0.5 5% modifier, constant temperature kneading stirring for 30 minutes to 2 hours; 3) adding bentonite quality 0.2 10% defoamer, constant temperature kneading stirring for 30 minutes to 2 hours; 4) the quality of bentonite 3 6% sodium modification agent, constant temperature kneading stirring for 30 minutes to 2 hours; when the use of bentonite as sodium bentonite, step 4) omitted; 5) 4) mixed material drying, crushing. The sodium bentonite exhibits better dispersity, suspension and colloid properties.
【技术实现步骤摘要】
一种钠基膨润土制备方法
本专利技术属于蒙脱石深加工领域，尤其涉及到一种易分散钠基膨润土及其制备方法。
技术介绍
粘土类产品因具有多种独特的优异性能，如滑爽性、吸附性、膨胀性，而被广泛应用于农业、轻工、冶金、化工、建材、机械、国防、环保等工业部门。在涂料涂装行业，随着国家对环境保护的日益重视，溶剂型涂料因其使用大量可挥发性溶剂，造成环境污染，而越来越多的被水性涂料替代，如水性工业涂料、水性建材涂料、水性家装涂料等等。在水性涂料行业，粘土类矿物作为一种良好的增稠、悬浮、触变、润滑剂受到广泛的关注，其中最受瞩目的材料为膨润土。膨润土矿在使用过程中一般需要进行提纯处理，提升蒙脱石含量。膨润土中蒙脱石的提纯主要采用湿法沉降提纯工艺，利用蒙脱石在水中易悬浮分散，比重轻的特点，将其他杂质矿物(如：石英、长石、方解石等)去除，达到提纯的目的。随着提纯设备的发展，蒙脱石的提纯方法由传统的重力沉降法，逐渐发展出水力旋流提纯，卧式螺杆离心提纯，碟片式离心提纯等具有更高效率的提纯工艺方法。上述几种方法一般统称为蒙脱石的湿法提纯工艺，在湿法提纯过程中，若加入无机钠盐(如：碳酸钠、氟化钠、焦...
【技术保护点】
一种钠基膨润土制备方法，其特征在于该方法包括以下步骤：1)将膨润土放入具有加热控温、捏合搅拌功能的反应器中，缓慢加入膨润土质量1‑10倍水，捏合搅拌，并升温加热至50‑80℃；2)加入膨润土质量0.5‑5％的表面修饰剂，恒温捏合搅拌30分钟～2小时；3)加入膨润土质量0.2‑10％的消泡剂，恒温捏合搅拌30分钟～2小时；4)将入膨润土质量3‑6％的钠化改性剂，恒温捏合搅拌30分钟～2小时；当所使用的膨润土为钠基膨润土时，步骤4)省略；5)将4)得到的混合物料烘干，粉碎；所述的表面修饰剂为阳离子型烷基酯基季铵盐、阳离子型瓜尔胶、阳离子型淀粉、阳离子型壳聚糖，或以上几种表面修饰...
【技术特征摘要】
1.一种钠基膨润土制备方法，其特征在于该方法包括以下步骤：1)将膨润土放入具有加热控温、捏合搅拌功能的反应器中，缓慢加入膨润土质量1-10倍水，捏合搅拌，并升温加热至50-80℃；2)加入膨润土质量0.5-5％的表面修饰剂，恒温捏合搅拌30分钟～2小时；3)加入膨润土质量0.2-10％的消泡剂，恒温捏合搅拌30分钟～2小时；4)将入膨...
【专利技术属性】
技术研发人员：王李广，
申请(专利权)人：天津金戈科技发展有限责任公司，
类型：发明
国别省市：天津,12