The present invention provides a method for mild preparation of graphene polyurethane sponge composite. The process comprises the following steps: 1. using the improved Hummers method to prepare graphene oxide; 2. with deionized water and cleaning water polyurethane sponge; graphene oxide solution 3. clean polyurethane sponge dipped in a certain concentration after drying in fully saturated, drying out to obtain graphene oxide polyurethane sponge; 4. graphene oxide polyurethane sponge immersed in sodium borohydride solution reduction, obtained the graphene polyurethane foam composite material. The process is simple, easy to operate, short time and small pollution to the environment. It is suitable for large-scale industrial production. The preparation of graphene polyurethane sponge has the characteristics of hydrophobic adsorption, in marine oil spill area has great application prospect.
【技术实现步骤摘要】
一种温和制备石墨烯-聚氨酯海绵复合材料的方法
本专利技术涉及在聚氨酯海绵上包覆一层石墨烯的方法，属于材料化学制备
技术介绍
随着石油的应用，在全球工业发展不断推进的同时，由原油泄漏和废油排放导致的海洋和河流污染问题也日渐突出。浮油和漏油污染，对水域生物系统带来了严重的灾害，油水液液分离成为世界范围内的研究热点。目前油水分离的主要方法有化学法，物理法和生物法。物理法中的吸附法因具有方便快捷，不易造成二次污染，对环境影响小，适合大规模浮油漏油回收处理的特点，而被广泛应用于海洋与河流的去油处理。然而，传统的吸油材料由于油水选择性差，吸油量低等弊端，使得废油回收和环境治理的效率大大降低。因此，开发与制备高性能吸油材料的问题亟待解决。聚氨酯海绵具有丰富的三维孔状结构，可以吸附和储存大量的油，特别是经过化学改性的聚氨酯海绵，具有疏水亲油的特点，可以快速实现油水分离，提高回收效率。目前，用石墨烯对聚氨酯海绵进行化学改性是研究的热点问题。然而，在制备石墨烯聚氨酯海绵过程中，往往以氧化石墨烯为原料，在还原氧化石墨烯的过程中大部分采用氢碘酸，水合肼，肼等具有强腐蚀性和高毒性...
【技术保护点】
一种温和制备石墨烯‑聚氨酯海绵复合材料的方法，其特征在于：利用硼氢化钠为还原剂在水热条件下温和地还原氧化石墨烯，该方法包括以下过程：1).制备氧化石墨烯，并配置氧化石墨烯水溶液；2).用去离子水清洗聚氨酯海绵并烘干；3).将清洗烘干后的聚氨酯海绵浸入步骤1)配置的氧化石墨烯水溶液中，充分浸透后，取出烘干获得氧化石墨烯‑聚氨酯海绵；4).将氧化石墨烯‑聚氨酯海绵浸入硼氢化钠溶液中，并置于水浴锅中还原，获得石墨烯‑聚氨酯海绵复合材料。
【技术特征摘要】
1.一种温和制备石墨烯-聚氨酯海绵复合材料的方法，其特征在于：利用硼氢化钠为还原剂在水热条件下温和地还原氧化石墨烯，该方法包括以下过程：1).制备氧化石墨烯，并配置氧化石墨烯水溶液；2).用去离子水清洗聚氨酯海绵并烘干；3).将清洗烘干后的聚氨酯海绵浸入步骤1)配置的氧化石墨烯水溶液中，充分浸透后，取出烘干获得氧化石墨烯-聚氨酯海绵；4).将氧化石墨烯-聚氨酯海绵浸入硼氢化钠溶液中，并置于水浴锅中还原，获得石墨烯-聚氨酯海绵复合材料。2.根据权利要求1所述的温和制备石墨烯-聚氨酯海绵复合材...
【专利技术属性】
技术研发人员：郭新立，刘园园，张伟杰，陈忠涛，赵丽，刘闯，祝龙，殷亮亮，金开，
申请(专利权)人：东南大学，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。