一种光固化快速成型中材料收缩的补偿方法及系统技术方案
A compensation method and system for material shrinkage in light curing rapid prototyping
The invention discloses a method and system for compensating a material stereolithography contraction, the method comprises: obtaining the first 3D model with preset aperture hole, according to the first model, the preparation of the first physical model; measuring the pore size of the first physical model, according to the measured value; the measured value and the preset aperture, calculated by the physical model of the first molding material shrinkage; according to the shrinkage rate, to compensate for the first physical model. The invention can realize the automatic compensation for the shrinkage of the molding material.
【技术实现步骤摘要】
一种光固化快速成型中材料收缩的补偿方法及系统
本专利技术涉及快速成型
，尤其涉及一种快速成型材料的收缩补偿方法及系统。
技术介绍
快速成型技术是利用计算机将三维模型数据分解成点或分解成面，再将材料由点堆积成面，由面叠积成体得到实体原型。目前快速成型技术有光固化快速成型、热熔融挤出成型以及选择性激光烧结三种主流方式，热熔融挤出成型以及选择性激光烧结得到的模型表面较为粗糙，精度低，而利用SLA/DLP光固化快速成型技术得到的模型表面光滑，精度较高，所以光固化快速成型技术得到了更多人的青睐。光固化快速成型技术所用的材料是液态光敏树脂，该种材料由液态固化变为固体时，存在一定的收缩率，导致得到的实体模型上的孔洞变小，与需要的孔径不相符，难以配合。针对该问题，目前的解决方式为，将成型出来的实体模型再经打磨以实现配合，但这种方式增加了相应的制作流程及工作量，效率较低。
技术实现思路
针对现有技术中的缺陷，本专利技术提供一种光固化快速成型中材料收缩的补偿方法及系统，可实现对材料收缩的自动补偿。第一方面，本专利技术提供了一种光固化快速成型中材料收缩的补偿方法，所述方法包括：获取带...
【技术保护点】
一种光固化快速成型中材料收缩的补偿方法，其特征在于，所述方法包括：获取带有预设孔径的孔的第一三维模型，根据所述第一三维模型，制备第一实物模型；测量所述第一实物模型中的孔径尺寸，得到测量值；根据所述测量值和所述预设孔径，计算得到第一实物模型的成型材料的收缩率；根据所述收缩率，对所述第一实物模型进行补偿。
【技术特征摘要】
1.一种光固化快速成型中材料收缩的补偿方法，其特征在于，所述方法包括：获取带有预设孔径的孔的第一三维模型，根据所述第一三维模型，制备第一实物模型；测量所述第一实物模型中的孔径尺寸，得到测量值；根据所述测量值和所述预设孔径，计算得到第一实物模型的成型材料的收缩率；根据所述收缩率，对所述第一实物模型进行补偿。2.根据权利要求1所述的补偿方法，其特征在于，所述根据所述第一三维模型，制备第一实物模型，具体包括：将所述第一三维模型切片，形成第一切片模型；以第一切片模型为基础，运用成型材料，逐层成型得到第一实物模型。3.根据权利要求1所述的补偿方法，其特征在于，所述根据所述收缩率，对所述第一实物模型进行补偿，具体包括：根据所述收缩率，扩大所述第一三维模型的孔径，得到第二三维模型；根据所述第二三维模型，制备第二实物模型。4.根据权利要求3所述的补偿方法，其特征在于，所述根据所述第二三维模型，制备第二实物模型，具体包括：将所述第二三...
【专利技术属性】
技术研发人员：林佳裕，李忠林，
申请(专利权)人：深圳晗竣雅科技有限公司，
类型：发明
国别省市：广东,44