本发明专利技术提供一种堆“埋弧焊熔敷金属试验”过渡层的焊接方法，根据所选焊剂碱度选取合适焊接参数，借助陶瓷衬垫，直接在试板侧面堆积过渡层。本发明专利技术可有效地降低熔敷金属试验劳动力成本、工作时间和机加工成本；比起传统的熔敷金属试验堆过渡层的方法，本发明专利技术的焊材消耗量明显减少。

A welding method for the transition layer of the pile \submerged arc welding metal test\

The invention provides a welding method for the transition layer of stacking \submerged arc welding deposited metal test\. According to the selected alkalinity of the flux, the suitable welding parameters are selected, and the transition layer is directly placed on the side of the test plate with ceramic backing. The invention can effectively reduce the labor cost, the deposited metal test time and machining cost; compared with traditional pile test of deposited metal transition layer, the invention of the welding material consumption decreased significantly.

【技术实现步骤摘要】
一种堆“埋弧焊熔敷金属试验”过渡层的焊接方法
本专利技术属于焊接
，特别涉及一种堆“埋弧焊熔敷金属试验”过渡层的焊接方法。
技术介绍
每种焊丝在焊丝生产厂家制作完成后和下游用户入厂前都要通过熔敷金属试验来检测其力学性能，而低合金埋弧焊丝在焊丝用量比例中接近一半，为此国外针对低合金埋弧焊丝的熔敷金属试验专门制定了标准AWSA5.23/A5.23M，而国内也制定了相对应的标准GB/T12470-2003。为了避免母材合金渗入对评判焊丝的性能产生的影响，熔敷金属试验开展前首先要选用配套的母材，然而低合金埋弧焊丝种类繁多，许多焊丝生产厂家并不一定有配套母材，标准规定：单边坡口角度为15°，如母材化学成分与熔敷金属化学成分不相当时，应用被检验的焊丝-焊剂组合或用相同类型的其他焊接材料，在坡口面及垫板面堆焊隔离层，隔离层厚度加工后不小于3mm。传统方法是先将母材开坡口，焊接间隙留有足够大，按照熔敷金属试验的焊接参数进行焊接，之后沿焊缝正中心对切开，并将试板铣平，然后在焊缝一侧开15°坡口，进行熔敷金属试验，见图1。但是此熔敷金属试验堆过渡层的方法使得熔敷金属试验工作量翻倍，且焊材消耗量和机本文档来自技高网...

【技术保护点】
一种堆“埋弧焊熔敷金属试验”过渡层的焊接方法，其特征在于：该方法包括以下步骤：(1)将焊接试板侧边向上竖起，两侧用厚钢块固定，试板两侧粘连陶瓷衬垫，并在试板上堆满焊剂；(2)焊剂碱度B，焊接速度v(m/h)，电流I(A)，电压U(V)，当B<1.0时，满足0.0005UI‑0.3v–3B＝0；当B≥1.0时，满足0.0004UI‑0.09v–B＝0，使焊缝熔宽为板厚20±0.3mm；(3)在试板上堆敷4层熔敷金属后，将试板两面铣平，在堆敷层上开15°坡口，使隔离层厚度加工后不小于3mm，并沿长度方向对切成两块焊板。

【技术特征摘要】
1.一种堆“埋弧焊熔敷金属试验”过渡层的焊接方法，其特征在于：该方法包括以下步骤：(1)将焊接试板侧边向上竖起，两侧用厚钢块固定，试板两侧粘连陶瓷衬垫，并在试板上堆满焊剂；(2)焊剂碱度B，焊接速度v(m/h)，电流I(A)，电压U(V)，当B&lt;1.0时...

【专利技术属性】
技术研发人员：王纳，郭慧英，陈刚，张宇，
申请(专利权)人：江苏省沙钢钢铁研究院有限公司，
类型：发明
国别省市：江苏,32