一种介孔表面缺陷Mn-N-TiO2微球光催化材料及其制备方法技术
A mesoporous surface defect Mn-N-TiO2 microsphere photocatalytic material and its preparation method
The invention relates to a mesoporous surface defect of Mn N TiO2 microspheres photocatalytic material and its preparing method. Including the preparation of mesoporous TiO2 microspheres surface defects of Mn and nitridation step, the nitrogen treatment with ammonia nitrogen source. The mesoporous surface defects of Mn TiO2 microspheres prepared by surfactant. Nitriding treatment in ammonia, obtain the mesoporous surface defects of Mn N TiO2 microsphere photocatalyst, photocatalytic materials of metal doped TiO2 double the experimental process of mesoporous spherical and homogeneous structure.
【技术实现步骤摘要】
一种介孔表面缺陷Mn-N-TiO2微球光催化材料及其制备方法
本专利技术涉及材料合成
，尤其涉及一种介孔表面缺陷Mn-N-TiO2微球光催化材料及其制备方法。
技术介绍
近年来，二氧化钛由于其低成本,可降解以及稳定的化学性质等特点在国内外已经引起了广泛关注,然而,二氧化钛由于其宽的带隙(3.2eV锐钛矿二氧化钛)以及载流子的快速复合使二氧化钛光催化剂的广泛应用是有限的。此外，仅吸收占不到太阳光5％的紫外光。这也极大地阻碍了其实际应用。因此，如何进一步提高TiO2的光催化活性已成为当前活跃的研究课题。对二氧化钛的改进经历了不同的阶段。首先进行TiO2本身的改进，研究者发现锐钛矿型二氧化钛具有更好的光催化效果。接下来是金属掺杂二氧化钛的时代，尤其以过渡金属掺杂的居多，但有报导称单一金属掺杂二氧化钛不具稳定性。紧接着又迎来了非金属掺杂二氧化钛的时代，B、C、F、N等阴离子掺杂二氧化钛不断被研究，但有报导称N掺杂有更稳定的光催化效果，为了拥有更好的光催化效果，金属非金属共掺杂的时代终于迎来了，huiyingwei在200年做了镧氮共掺杂二氧化钛的相关研究；YeCon...
【技术保护点】
一种介孔表面缺陷Mn‑N‑TiO2微球光催化材料，其特征在于：包括制备介孔表面缺陷的Mn‑TiO2微球和氮化处理步骤，所述氮化处理所用氮源为氨气。
【技术特征摘要】
1.一种介孔表面缺陷Mn-N-TiO2微球光催化材料，其特征在于：包括制备介孔表面缺陷的Mn-TiO2微球和氮化处理步骤，所述氮化处理所用氮源为氨气。2.根据权利要求1所述的光催化材料，其特征在于：所述介孔表面缺陷的Mn-TiO2微球制备中加入表面活性剂。3.一种介孔表面缺陷Mn-N-TiO2微球光催化材料的制备方法，其特征在于：所述方法包括：将表面活性剂溶于乙醇溶液中，搅拌一段时间表面活性剂充分溶解后，加入含锰化合物的乙醇溶液，加入水，调低磁力搅拌转数，最后快速加入含钛化合物，搅拌后静置沉降，乙醇和/或水洗涤3次以上，干燥研磨得粉末，之后将粉末进行水热反应，将所得的产物在空气气氛中煅烧一段时间，再进行高温氮化处理，制备得到介孔表面缺陷Mn-N-TiO2微球光催化材料。4.根据权利要求3所述的制备方法，其特征在于：表面活性剂与含钛化合物摩尔比为(0.1-2):1；表面活性剂与含钛化合物优选摩尔比为(0.2-2):1，最佳为0.5：1；所述含锰化合物包括：乙酸锰，氯化锰或硫酸锰中的一种或两种以上；所述含钛化合物为异丙醇钛、四氯化钛或硫酸氧钛中的一种或两种以上；所述表面活性剂为十六胺、十八胺或十二烷基磺酸钠中的一种或两种以上，在静置之前的操作步骤中，反应体系中加...
【专利技术属性】
技术研发人员：杨明辉，冯璐，邹明明，刘红红，
申请(专利权)人：中国科学院大连化学物理研究所，
类型：发明
国别省市：辽宁,21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。