一种成品太阳能电池退火的方法技术
A method of annealing of finished solar cells
The invention discloses a method, a product of solar cell annealing include: setting each interval chain annealing furnace temperature and furnace with speed; the chain annealing furnace air discharge; hydrogen and nitrogen is introduced into the chain type annealing furnace; the finished solar cells placed in the chain the annealing furnace feeding furnace at the transfer zone; in the chain type annealing furnace annealing after hydrogenation preset time after feeding at removing the finished solar cell from the chain under the annealing furnace. The annealing method of the finished solar cells can reduce the time of hydrogenating annealing process, improve the efficiency of solar cells, reduce the defects in solar cells, enhance the open circuit voltage of batteries, and improve the conversion efficiency.
【技术实现步骤摘要】
一种成品太阳能电池退火的方法
本专利技术属于光伏设备制造
，特别是涉及一种成品太阳能电池退火的方法。
技术介绍
由于太阳能电池级硅材料中不可避免的含有大量的杂质和缺陷，导致硅中少子寿命及扩散长度降低，从而影响电池的转换效率。氢(H)能与硅中的缺陷或杂质进行反应，起到钝化的作用，因此现有一种氢化退火技术，具体的，是通过氢钝化提升硅片电池表面的钝化效果，从而提升晶硅电池的开路电压，达到效率提升的目的。现有的氢化退火技术方案是利用石墨舟承载硅片的管式量产机台，将PECVD镀膜后，丝网印刷前的硅片置于450°左右的N2和H2混合气体中进行一定时间的退火，达到氢钝化的目的。现有的技术方案缺陷包括：这是针对丝网印刷前PECVD镀膜后的半成品电池片进行退火处理，使用石墨舟承载硅片的管式量产机台，上料下料操作复杂，且工艺开始前需对炉管进行升温和氮气吹扫，结束后需抽真空和氮气再次吹扫，避免炉管有其他气体残留，造成安全隐患，工艺运行时间较长(60min)，影响部分产能。
技术实现思路
为解决上述问题，本专利技术提供了一种成品太阳能电池退火的方法，能够减少氢化退火工艺的时间，在提高效...
【技术保护点】
一种成品太阳能电池退火的方法，其特征在于，包括：设置链式退火炉内各个区间的温度以及炉带移动速度；将所述链式退火炉内的空气排出；向所述链式退火炉内通入氢气和氮气；将成品太阳能电池放置在所述链式退火炉的上料处的传送炉带上；在所述链式退火炉内经过预设时间的氢化退火后，从所述链式退火炉的下料处取出所述成品太阳能电池。
【技术特征摘要】
1.一种成品太阳能电池退火的方法，其特征在于，包括：设置链式退火炉内各个区间的温度以及炉带移动速度；将所述链式退火炉内的空气排出；向所述链式退火炉内通入氢气和氮气；将成品太阳能电池放置在所述链式退火炉的上料处的传送炉带上；在所述链式退火炉内经过预设时间的氢化退火后，从所述链式退火炉的下料处取出所述成品太阳能电池。2.根据权利要求1所述的成品太阳能电池退火的方法，其特征在于，所述设置链式退火炉内各个区间的温度为：设置所述链式退火炉各个区间的温度为100℃至450℃。3.根据权利要求1所述的成品太阳能电池退火的方法，其特征在于，所述设置链式退火炉的炉带移动速度为：设置链式退火炉的炉带移动速度为10inch/min至30inch/min。4.根...
【专利技术属性】
技术研发人员：侯玥玥，金井升，张昕宇，金浩，黄纪德，
申请(专利权)人：浙江晶科能源有限公司，晶科能源有限公司，
类型：发明
国别省市：浙江,33