一种氮化物改性氧化铝磨料及其生产工艺制造技术
A nitride modified alumina abrasive and its production process
A nitride modified alumina abrasive and its production process, including alumina 90 ~ 99%, 0.5 ~ 2% nitride, oxide modified 0 ~ 9.5% steps: S1, mixing the raw materials: aluminum oxide powder, nitride and modified mixed oxide; S2, melting the mixture is added to high temperature melting in arc furnace, S3; cooling: poured in the package barrel, with conventional cooling, or rapid cooling; S4, crushing and screening: cooling solidification materials after crushing and screening into abrasive particles. The invention has the beneficial effects of directly adding nitrides in corundum smelting, greatly reduce the energy consumption; the production cost is low; the grinding performance is brown corundum and white corundum is obviously improved, suitable for cutting, grinding, shutter, sandpaper and vitrified grinding wheel.
【技术实现步骤摘要】
一种氮化物改性氧化铝磨料及其生产工艺
本专利技术属于磨料领域，具体为一种氮化物改性氧化铝磨料及其生产工艺。
技术介绍
从1891年专利技术人造磨料以来，电熔刚玉的品种主要是棕刚玉、白刚玉、单晶刚玉、铬刚玉和锆刚玉，它们于20世纪纷纷得到了产业化应用，然而自20世纪80年代以后，很少有新的电熔刚玉专利技术。目前中国电熔刚玉的产能虽然超过世界需求2倍以上，但是95%以上都是生产技术落后的棕刚玉和白刚玉，因此急需新产品进行升级转型。氮化物或者氮氧化物改性的氧化铝磨料在做耐火材料时，钢铁材料对它的浸润性很差，就是说氮化物或者氮氧化物改性的氧化铝在高温磨削过程中会不粘钢铁屑，可以提高磨削性能。美国专利US5023212描述了一种新型电熔刚玉，主要由氧化铝、碳氧化铝和氮氧化铝多相材料组成，其中，氧化铝材料形成刚玉基体，微晶相的碳氧化铝、氮氧化铝和碳氮氧化铝均匀地分散在其中，碳含量在0.05-5%之间，氮含量在0.05-5%之间。该材料的生产通过加碳和在氧化铝熔体中喷入氮气而得，该生产工艺的主要缺点是因要喷入氮气而导致耗能大，如其专利实施例所述，每吨磨料能耗约1万度电，而普通棕...
【技术保护点】
一种氮化物改性氧化铝磨料，其特征在于，其包括如下重量百分含量的原料：氧化铝90～99%，氮化物0.5～2%，改性氧化物0～9.5%。
【技术特征摘要】
1.一种氮化物改性氧化铝磨料，其特征在于，其包括如下重量百分含量的原料：氧化铝90～99%，氮化物0.5～2%，改性氧化物0～9.5%。2.根据权利要求1所述的一种氮化物改性氧化铝磨料，其特征在于，所述氮化物为氮化铝或氮化硅。3.根据权利要求1所述的一种氮化物改性氧化铝磨料，其特征在于，所述改性氧化物为二氧化钛、氧化锆、氧化镁、稀土氧化物、氧化锶、氧化钡、氧化铁、氧化锰或氧化钴中的一种或两种以上任意比例的组合物。4.一种氮化物改性氧化铝磨料的生产工艺，其特征在于，其工艺步骤如下：S1、原料混合：将氧化铝粉、氮化物和改性氧化物混合；S2、熔化：将混合物加入电弧炉中高温熔化；S3、冷却：熔化后倒入接包桶或其它冷却...
【专利技术属性】
技术研发人员：王胜国，牛耀武，郭志邦，禄清，
申请(专利权)人：郑州威源新材料有限公司，
类型：发明
国别省市：河南,41