The invention discloses a preparation method of thermal insulation mortar, comprises the following raw group weight: 80 slag powder 90, attapulgite 4 6 copies, 80 copies, 70 Portland cement waste polystyrene foam, 8 10 SM melamine superplasticizer 0.7 1, jade 7 powder 9, sodium tripolyphosphate 1 2 copies, 3 copies, 2 pentaerythritol 0.1 calcium gluconate 0.2, barium stearate 2, 1 bisphenol A phosphite 1 2 copies, 3 copies of B-naphthol 2, two 0.1, 0.07 methyl silicone oil modified additives 5 7, amount of water, sand slurry insulation production by using slag powder and waste polystyrene foam and other solid waste, reduce the pollution of the environment, it can replace part of cement, saving energy, good insulation performance, safety and environmental protection, non-toxic side effects.
【技术实现步骤摘要】
一种保温砂浆的制备方法
本专利技术涉及一种保温砂浆的制备方法。
技术介绍
保温砂浆是以各种轻质材料为骨料，以水泥为胶凝料，掺和一些改性添加剂，经生产企业搅拌混合而制成的一种预拌干粉砂浆。主要用于建筑外墙保温，具有施工方便、耐久性好等优点。建筑工业在国民经济中占有重要地位。纵观各工业，能耗大、浪费严重、节约潜能最大的工业当属建筑行业，近年来，大规模利用固体废弃物生产的新型建材，一方面解决了固体废弃物出路问题，另一方面随着新型建材的广泛应用，在节能、节地、利废和环境保护等方面都取得了成功，受到人们的普遍欢迎。因此，利用固体废弃物制备保温砂浆的研究值得探讨。
技术实现思路
专利技术目的：提供一种利用固体废弃物制备的保温砂浆。技术方案：一种保温砂浆的制备方法，其特征在于包括如下以重量计算的原料组分：矿渣粉80-90份、凹凸棒土4-6份、硅酸盐水泥70-80份、废弃聚苯乙烯泡沫8-10份、三聚氰胺SM高效减水剂0.7-1份、玉石粉7-9份、三聚磷酸钠1-2份、季戊四醇2-3份、葡萄糖酸钙0.1-0.2份、硬脂酸钡1-2份、亚磷酸双酚A酯1-2份、乙萘酚2-3份、二甲基硅油0.0...
【技术保护点】
一种保温砂浆的制备方法，其特征在于包括如下以重量计算的原料组分：矿渣粉80‑90份、凹凸棒土4‑6份、硅酸盐水泥70‑80份、废弃聚苯乙烯泡沫8‑10份、三聚氰胺SM高效减水剂0.7‑1份、玉石粉7‑9份、三聚磷酸钠1‑2份、季戊四醇2‑3份、葡萄糖酸钙0.1‑0.2份、硬脂酸钡1‑2份、亚磷酸双酚A酯1‑2份、乙萘酚2‑3份、二甲基硅油0.07‑0.1份、改性助剂5‑7份、水适量。
【技术特征摘要】
1.一种保温砂浆的制备方法，其特征在于包括如下以重量计算的原料组分：矿渣粉80-90份、凹凸棒土4-6份、硅酸盐水泥70-80份、废弃聚苯乙烯泡沫8-10份、三聚氰胺SM高效减水剂0.7-1份、玉石粉7-9份、三聚磷酸钠1-2份、季戊四醇2-3份、葡萄糖酸钙0.1-0.2份、硬脂酸钡1-2份、亚磷酸双酚A酯1-2份、乙萘酚2-3份、二甲基硅油0.07-0.1份、改性助剂5-7份、水适量。2.根据权利要求1所述的保温砂浆的制备方法，其特征在于：所述改性助剂由如下以重量计算的原料组成：红土40-65份、骨粉2-4份、蜂胶3-5份、磷酸二氢铝3-4份、可...
【专利技术属性】
技术研发人员：肖护兵，张玉贞，柳卫军，
申请(专利权)人：江苏天诺环境工程技术开发有限公司，
类型：发明
国别省市：江苏,32