The invention discloses a preparation method of dye wastewater treatment using polyvinyl formal active carbon porous composite material and its preparation, which is characterized in that to add distilled water in PVA, water bath heating and stirring, polyvinyl alcohol water solution clarification; a polyvinyl alcohol solution of water bath heating, adding borax solution after reaction with urea and hydrogen peroxide, the mixed reaction of ferrous sulfate, phosphoric acid butyl ester three, stirring hydrophobic modified polyvinyl alcohol glue; to the other a polyvinyl alcohol aqueous solution, adding dilute sulfuric acid, formaldehyde and expanded graphite, mixing reaction, in situ synthesis of polyvinyl formal composite; polyvinyl formal to compound, adding starch, glycerol, heating and stirring to dissolve, get sticky the liquid, adding activated carbon, OP 10, n-pentane and hydrophobic modified polyvinyl alcohol glue, rapid stirring mixing Well, the viscous liquid into the evaporating dish into the oven, heating, get activated carbon composite porous polyvinyl formal.
【技术实现步骤摘要】
一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料及其制备方法
本专利技术涉及多孔复合材料领域,具体涉及一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料及其制备方法。
技术介绍
染料废水中存在大量的有机污染物和无机污染物,未经处理排放会破坏水体生态平衡,影响水生生物和微生物的生存,无法进行生物降解,使环境恶化,会通过饮用水和食物链传递给人类,最终会严重危害人类的健康。所以,处理染料废水的很紧迫且必要。
技术实现思路
本专利技术主要解决的技术问题是提供一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料及其制备方法,依照该工艺制备的多孔复合材料具有良好的吸附性能和防水性能。本专利技术所要解决的技术问题采用以下的技术方案来实现:一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料的制备方法,其特征在于,按以下步骤进行:a.向30-40重量份聚乙烯醇中1:10-15加入蒸馏水,升温至90-100℃水浴加热搅拌1-2h,得到澄清的聚乙烯醇水溶液,均分成两份,待用;b.将a中所得一份聚乙烯醇溶液水浴加热至70-80℃,搅拌下加入2-3重量份硼砂溶液,恒温搅拌反应1-2h后,与1-2重量份尿素、0.1-0.3重量份双氧水混合,搅拌均匀,用1-2mol/L的HCl调pH为5-6,加0.1-0.2重量份硫酸亚铁,保温50-60℃搅拌反应30-50min,滴加0.1-0.2重量份磷酸三丁酯,搅拌均匀,冷却至室温,调pH为中性,得疏水改性聚乙烯醇胶液;c.向a中所得另一份聚乙烯醇水溶液中,加入5-10重量份稀硫酸、10-15重量份甲醛和2-4重量份膨胀石墨,控制反应温度为6 ...
【技术保护点】
一种染料废水处理用聚乙烯醇缩甲醛‑活性炭多孔复合材料的制备方法,其特征在于:向聚乙烯醇中加蒸馏水,水浴加热搅拌,得澄清的聚乙烯醇水溶液;将一份聚乙烯醇溶液水浴加热,加硼砂溶液反应后,与尿素、双氧水、硫酸亚铁混合反应,加磷酸三丁酯,搅拌得疏水改性聚乙烯醇胶液;向另一份聚乙烯醇水溶液中,加入稀硫酸、甲醛和膨胀石墨,搅拌反应,原位合成聚乙烯醇缩甲醛复合物;向聚乙烯醇缩甲醛复合物中,加淀粉、甘油,加热搅拌溶解,得到粘稠状的液体,加活性炭、OP‑10、正戊烷及疏水改性聚乙烯醇胶液,快速搅拌均匀,将粘稠液体倒入蒸发皿中,放入烘箱内加热,得到聚乙烯醇缩甲醛‑活性炭多孔复合材料。
【技术特征摘要】
1.一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料的制备方法,其特征在于:向聚乙烯醇中加蒸馏水,水浴加热搅拌,得澄清的聚乙烯醇水溶液;将一份聚乙烯醇溶液水浴加热,加硼砂溶液反应后,与尿素、双氧水、硫酸亚铁混合反应,加磷酸三丁酯,搅拌得疏水改性聚乙烯醇胶液;向另一份聚乙烯醇水溶液中,加入稀硫酸、甲醛和膨胀石墨,搅拌反应,原位合成聚乙烯醇缩甲醛复合物;向聚乙烯醇缩甲醛复合物中,加淀粉、甘油,加热搅拌溶解,得到粘稠状的液体,加活性炭、OP-10、正戊烷及疏水改性聚乙烯醇胶液,快速搅拌均匀,将粘稠液体倒入蒸发皿中,放入烘箱内加热,得到聚乙烯醇缩甲醛-活性炭多孔复合材料。2.一种染料废水处理用聚乙烯醇缩甲醛-活性炭多孔复合材料的制备方法,其特征在于:a.向30-40重量份聚乙烯醇中1:10-15加入蒸馏水,升温至90-100℃水浴加热搅拌1-2h,得到澄清的聚乙烯醇水溶液,均分成两份,待用;b.将a中所得一份聚乙烯醇溶液水浴加热至70-80℃,搅拌下加入2-3重量份硼砂溶液,恒温搅拌反应1-2h后,与1-2重量份尿素、0.1-0.3重量份双氧水混合,搅拌均匀,用1-2mol...
【专利技术属性】
技术研发人员:汪义卉,
申请(专利权)人:马鞍山科信网络科技有限公司,
类型:发明
国别省市:安徽,34