一种提高EPDM粘合力的帆布结构制造技术
A canvas structure to improve the EPDM adhesion
The utility model discloses a canvas structure for improving the adhesion force of EPDM, which comprises a plurality of warps and multiple weft yarns, each warp and weft yarn are cross braided, and each two warp yarns and two weft yarns are kept at intervals. The utility model fabric structure formed by the warp and weft weaving, and keep every two warp spacing and two weft spacing, rubber vulcanization can penetrate, rubber and rubber compatibility better, improve the adhesion between the rubber, to prevent delamination and delay aging, improve service life that effectively solves problems in the prior art closely spaced weft warp lead to the infiltration of glue, easy delamination and short life of aging and use, the utility model has the advantages of simple structure and low cost.
【技术实现步骤摘要】
一种提高EPDM粘合力的帆布结构
本技术涉及一种提高EPDM(三元乙丙胶)粘合力的帆布结构，属于产业织物的
技术介绍
EPDM橡胶活性比较低，与VP胶乳浸胶液之间的粘合比较差，现有的帆布织物结构紧密排列，橡胶硫化时，帆布织物结构两侧的橡胶相互间几乎不渗透，仅靠帆布织物表面的浸胶液与两侧的EPDM橡胶结合，粘合性差，易老化脱层，使用寿命短。
技术实现思路
本技术要解决的技术问题是：提供一种提高EPDM粘合力的帆布结构，输送带在硫化时两侧橡胶通过帆布经纬交叉之间的空隙能相互渗透自粘，提高粘合性，防止脱层和延迟老化，提高使用寿命，以解决现有技术中存在的问题。本技术采取的技术方案为：一种提高EPDM粘合力的帆布结构，包括多条经纱和多条纬纱，每条经纱和纬纱交叉编织，每两条经纱和每两条纬纱间分别保持间隔。优选的，上述每两条经纱间间距为0.4-0.6mm。优选的，上述每两条纬纱间间距为0.4-0.6mm。优选的，上述经纱细度为3000D-7000D，纬纱细度为2000-4000D。优选的，上述经纱线密度60-80根/10厘米，纬纱线密度60-70根/10厘米。本技术的有益效果：与现有技术相比，本技术的帆布织物结构通过经纱和纬纱交叉编织而成，并保持每两条经纱间间距和两条纬纱间间距，输送带在硫化时两侧橡胶通过帆布经纬交叉之间的空隙能相互渗透自粘，橡胶与橡胶间相容性更好，提高橡胶间的粘合性，防止脱层和延迟老化，提高使用寿命，有效解决了现有技术中存在的紧密排列的经纱纬纱导致的无法渗透胶液、易脱层和老化、使用寿命短的问题，本技术还具有结构简单、成本低的特点。附图说明图1是本...
【技术保护点】
一种提高EPDM粘合力的帆布结构，其特征在于：包括多条经纱（1）和多条纬纱（2），每条经纱（1）和纬纱（2）交叉编织，每两条经纱（1）和每两条纬纱（2）间分别保持间隔；每两条经纱（1）间间距为0.4‑0.6mm；每两条纬纱（2）间间距为0.4‑0.6mm。
【技术特征摘要】
1.一种提高EPDM粘合力的帆布结构，其特征在于：包括多条经纱（1）和多条纬纱（2），每条经纱（1）和纬纱（2）交叉编织，每两条经纱（1）和每两条纬纱（2）间分别保持间隔；每两条经纱（1）间间距为0.4-0.6mm；每两条纬纱（2）间间距为0.4-0.6mm。2.根据权利要求1...
【专利技术属性】
技术研发人员：翁中华，吴增华，李勇，赵顺章，孙希家，
申请(专利权)人：浙江尤夫科技工业有限公司，
类型：新型
国别省市：浙江,33