The invention provides a preparation process for fiber - opening fabric, which belongs to the field of textile fabric. It is carried out according to the following process: grey cloth, buckets, desizing (desizing + slack), opening fiber, dyeing, dehydration, finishing and setting. The preparation process of the present invention provides a fine fiber fabric, the fabric has high density and light, with a soft hand and other functions, to overcome the fine fabrics market on easily with static electricity, warp, fuzz, uneven dyeing, color etc.. In addition, the invention has the advantages of simple process and easy operation.
【技术实现步骤摘要】
一种开纤面料的制备工艺
本专利技术涉及一种面料制备工艺，尤其涉及一种开纤面料的制备工艺。
技术介绍
超细旦锦纶纤维或涤纶纤维是近几年兴起的一种新型的纺织原料，与天然纤维相比，具有高强、耐磨、回弹好等优良的物理机械性能，高密、质轻，具有柔软的手感，适宜做休闲服面料。但是因其纱旦较细，织造环节容易造成效率低、品质差、断经、毛丝的问题，在染色过程中，容易造成布面不均匀、色花、色牢度差等问题。
技术实现思路
针对现有技术的不足，本专利技术所要解决的技术问题提供一种开纤面料的制备工艺，采用如下方案：一种开纤面料的制备工艺，其按如下流程进行：坯布→配桶→退浆（退浆+松弛）→开纤→染色→脱水→整理定型。进一步的，所述坯布，经纱采用20D超细旦锦纶或涤纶纤维，纬纱采用20D超细旦涤纶、锦纶或45D涤锦复合丝为原料，在进口津田驹喷水织机上制织而成，产品经纬总密度1365~1565根/10cm。进一步的，所述退浆工艺处理，组成部分按重量分为：退浆剂M-1011K：8-10g/L；渗透剂M-7705或M-1038C：1-2g/L；纯碱：1-2g/L。优选的，所述退浆工序按如下流程：润湿98...
【技术保护点】
一种开纤面料的制备工艺，其特征在于所述生产工艺流程按如下进行：坯布→配桶→退浆（退浆+松弛）→开纤→染色→脱水→整理定型。
【技术特征摘要】
1.一种开纤面料的制备工艺，其特征在于所述生产工艺流程按如下进行：坯布→配桶→退浆（退浆+松弛）→开纤→染色→脱水→整理定型。2.根据权利要求1所述的一种开纤面料的制备工艺，其特征在于所述坯布经纱采用20D超细旦锦纶或涤纶纤维，纬纱采用20D超细旦涤纶、锦纶或45D涤锦复合丝为原料，在进口津田驹喷水织机上制织而成，产品经纬总密度1365~1565根/10cm。3.根据权利要求1所述的一种开纤面料的制备工艺，其特征在于所述退浆工艺处理，组成部分按重量分为：退浆剂M-1011K：8-10g/L；渗透剂M-7705或M-1038C：1-2g/L；纯碱：1-2g/L,所述退浆工序按如下流程：润湿98℃→退浆98℃→皂洗90℃~80℃→清水洗70℃~50℃，车速控制在50m/min。4.根据权利要求1所述的一种开纤面料的制备工艺，其特征在于开纤工艺组成部分按重量分为：烧碱浓度：4.0-6.0g/L...
【专利技术属性】
技术研发人员：刘宁宁，张浩珍，
申请(专利权)人：苏州鸣珮新材料有限公司，
类型：发明
国别省市：江苏,32