一种硬质合金生产用成型剂制造技术

本发明专利技术公开了一种新的硬质合金生产用成型剂，由质量百分比为30%~70%的硬脂酸、70%~30%的聚氨酯树脂组成；将上述成型剂按照一定的比例，与硬质合金粉末原料以及酒精湿磨介质共同球磨混合，得到均匀的硬质合金混合料料浆；然后通过喷雾干燥工艺得到流动性较好的含有上述成型剂的硬质合金混合料，再将混合料压制成型，烧结得到硬质合金产品；本成型剂成分简单，成型性能好，可完全溶于酒精，适合喷雾干燥工艺，残留碳量低，且安全环保，适合硬质合金大批生产的新型成型剂。

A molding agent for the production of hard alloy

The present invention discloses a new kind of plasticizer production of hard alloy, composed of mass percentage of 30%~70% polyurethane resin, stearic acid, 70%~30%; the forming agent according to a certain proportion, and the hard alloy powder as raw material and alcohol wet grinding medium common milling mixing, get hard alloy mixed slurry; and through the spray drying process has fluidity of cemented carbide mixture containing the forming agent better, then the mixture is pressed, sintered hard alloy products; the forming agent composition is simple, forming a good performance, can be completely dissolved in alcohol, suitable for spray drying process, the residual carbon content is low, and the safety and environmental protection, new forming agent for the production of a large number of hard alloy.

【技术实现步骤摘要】
一种硬质合金生产用成型剂
本专利技术涉及一种用于粉末冶金生产的成型剂，尤其是适用于硬质合金生产的成型剂。
技术介绍
在硬质合金生产过程中，为了使粉末压制成各种形状的产品，必须向硬质合金混合料中添加一定量的成型剂来改善混合料的压制成型性能，并增加硬质合金生坯的强度。目前硬质合金行业所用的成型剂主要分为三类。第一类是聚乙二醇(PEG)型，第二类是石蜡型，第三类是橡胶型，如顺丁橡胶、丁纳橡胶及丁苯橡胶等。这三类成型剂各有特点，PEG的优点是残留碳量低，于酒精互溶，适合现代先进化的喷雾干燥工艺，缺点是成形性能不理想，混合料吸湿，受环境影响大。石蜡的优点是残留碳量很少，可以进行喷雾干燥，缺点是不溶于酒精，成形性能差，压坯强度低。橡胶的优点是成型性能优良，能生产形状复杂的产品，缺点是残留碳量高，易老化，不溶于酒精，不适合进行喷雾干燥工艺。因此针对硬质合金生产用成型剂有很多研究与改进，包括专利。如“一种硬质合金成型蜡”（公告号CN103897408B）以石蜡，十八醇及蜂蜡为原料，成型性能相比石蜡有所改善，但仍旧不适用于喷雾干燥工艺，且其成分复杂。如“一种硬质合金成型剂及其生产制备方法”（公告号CN本文档来自技高网...

【技术保护点】
一种硬质合金生产用成型剂，由质量百分比为30%~70%的硬脂酸、70%~30%的聚氨酯树脂组成。

【技术特征摘要】
1.一种硬质合金生产用成型剂，由质量百分比为30%~70%的硬脂酸、70%~30%的聚氨酯树脂组成。2.如权利要求1所述一种硬质合金生产用成型剂，其特征在于：硬脂酸的质量百分比为30%，聚氨酯树脂的质量百分比为70%。3.如权利要求1所述一种硬质合金生产用成型剂，其特征在于：硬脂酸的质量百分比为40%，聚氨酯树脂的质量百分比为60%。4.如权...

【专利技术属性】
技术研发人员：洪海侠，孟小卫，汪巍，
申请(专利权)人：株洲硬质合金集团有限公司，
类型：发明
国别省市：湖南,43