A reed compression plate making method, mainly in the following: first, production of raw materials: reed, glass fiber, polyurethane glue, nails dry; two, making tools: heating machine, molding machine; three, the harvest of reed Liangshai drying to harden, adding polyurethane glue, adding amount of 25KG/200KG. Stir the mixture evenly, static absorption 2~3 hours after collection of bottom glue reuse; four, will be absorbed into the polyurethane glue reed making good mould plate, a compression lid mold cover, heating 3~4 minutes, setting a heating temperature of 150 DEG C to 200 c, five, will be finalized; heated mold from the hot material together with cooling to 30 DEG C, after forming, demoulding, on plate surface voids where excessive polyurethane glue for repair.
【技术实现步骤摘要】
一种芦苇杆压缩板的制作方法
本专利技术涉及一种压缩板的制作方法，特别涉及以芦苇杆作为原料的压缩板的制作方法，属于新材料加工
技术介绍
芦苇，多年水生或湿生的高大禾草，生长在灌溉沟渠旁、河堤沼泽地等，世界各地均有生长，芦叶、芦花、芦茎、芦根、芦笋均可入药。芦苇的果实为颖果，披针形，顶端有宿存花柱。具长、粗壮的匍匐根状茎，以根茎繁殖为主，芦苇是经常见到的水边植物或干枯的水塘里，芦苇常会和寒芒搞混，区别是芦苇的茎是中空的，而寒芒不是，另外，寒芒到处可见，芦苇是择水而生。芦茎、芦根还可以用于造纸行业，以及生物制剂。经过加工的芦茎还可以做成工艺品。多年水生或湿生的高大禾草，生长在灌溉沟渠旁、河堤沼泽地等。芦苇的植株高大，地下有发达的匍匐根状茎。茎秆直立，秆高1～3米，节下常生白粉。叶鞘圆筒形，无毛或有细毛。叶舌有毛，叶片长线形或长披针形，排列成两行。叶长15-45厘米，宽1-3．5厘米。圆锥花序分枝稠密，向斜伸展，花序长10一40cm，小穗有小花4—7朵；颖有3脉，一颖短小，二颖略长；第一小花多为雄性，余两性；第二外样先端长渐尖，基盘的长丝状柔毛长6—12mm；内...
【技术保护点】
一种芦苇杆压缩板的制作方法，其特征是按下面的制作进行：一、原料：干燥的芦苇、聚氨酯胶水、玻璃纤维、铁钉；二、制作工具：模压机、加热机；三、将芦苇收割凉晒干燥至变硬，加入聚氨酯胶水，加入量25KG/200KG，搅拌调和均匀，静置吸收2~3个小时后收集底部胶水再利用；四、将吸收了聚氨酯胶水的芦苇放进制作好的板式模具中，稍作压缩，合盖模盖，加热3~4分钟，加热温度150℃~200℃，定型；五，将加热定型的模具材料一起脱离加热点后降温至30℃以下，定型后脱模，对板材表面空隙过大的地方用聚氨酯胶水修补。
【技术特征摘要】
1.一种芦苇杆压缩板的制作方法，其特征是按下面的制作进行：一、原料：干燥的芦苇、聚氨酯胶水、玻璃纤维、铁钉；二、制作工具：模压机、加热机；三、将芦苇收割凉晒干燥至变硬，加入聚氨酯胶水，加入量25KG/200KG，搅拌调和均匀，静置吸收2~3个小时后收...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。