本发明专利技术提供一种新型防刺防割服装面料，涉及纺织材料技术领域，包括外表层、间隔层和内表层，所述外表层为防护层，所述防护层由芳纶包缠纱构成，所述外表层为密实结构；所述内表层为舒适层，所述内表层为网眼结构；所述间隔层采用经编间隔织物组织，所述间隔层内填充剪切增稠液。本发明专利技术提高面料的抗刺抗刀割能力，同时解决面料柔软性差，手感硬，面料舒适性不好的问题。

A new type of anti prickly and anti cutting garment fabric

The invention provides a novel anti stab cut fabric, which relates to the technical field of textile materials, including surface layer, interlayer and inner surface, the outer layer is a protective layer, the protective layer is made of aramid yarn, the outer layer is a compact structure; the inner surface is comfortable the inner layer, the surface mesh structure; the interlayer uses the warp knitted spacer fabric, the spacer layer thickening liquid filled shear. The invention improves the resistance to cutting and cutting of the fabric, and solves the problem of poor fabric softness, hard feel and bad comfortability of the fabric.

【技术实现步骤摘要】
一种新型防刺防割服装面料
本专利技术涉及纺织材料
，具体涉及一种新型防刺防割服装面料。
技术介绍
面料就是用来制作服装的材料，作为服装三要素之一，面料不仅可以诠释服装的风格和特性，而且直接左右着服装的色彩、造型的表现效果。随着人们生活水平和文化品位的日益提高，着装理念也发生了新的变化，由过去传统的注重结实耐穿、防寒保暖到转变为当今的崇尚时尚自由、运动休闲，强调环保抗污染、保健、舒适合体、随意自然又美丽大方的服装。随着高科技的迅猛发展，新材料、新技术和新工艺被大量应用到衣服面料上，因而出现了抗菌防螨、吸热保温、抗紫外线、防水防静电、吸汗透湿、耐火阻燃等形形色色的功能性服装面料。因此，无论在工作还是生活中，功能性面料将成为人们不可缺少的亲密助手。目前市场上常见的防刺防割面料主要有硬质和软质两种。硬质防刺防割面料采用金属丝、金属网等刚性材料实现防护功能，存在重量大、灵活性差、防刺性能各向均匀性不好、个别方向防刺性能差等缺点；轻质防刺防割面料主要采用高强高模的芳纶纤维和超高分子量聚乙烯纤维，将其织物、无纺布或涂层织物复合制成面料层，起到防刀割防磨损的作用，但是其成本偏高，而且由于防护面本文档来自技高网...

【技术保护点】
一种新型防刺防割服装面料，其特征在于，包括外表层、间隔层和内表层，所述外表层为防护层，所述防护层由芳纶包缠纱构成，所述外表层为密实结构；所述内表层为舒适层，所述内表层为网眼结构；所述间隔层采用经编间隔织物组织，所述间隔层内填充剪切增稠液。

【技术特征摘要】
1.一种新型防刺防割服装面料，其特征在于，包括外表层、间隔层和内表层，所述外表层为防护层，所述防护层由芳纶包缠纱构成，所述外表层为密实结构；所述内表层为舒适层，所述内表层为网眼结构；所述间隔层采用经编间隔织物组织，所述间隔层内填充剪切增稠液。2.根据权利要求1所述的一种新型防刺防割服装面料，其特征在于，所述芳纶包缠纱包括芯纱和螺旋状缠绕在所述芯纱上的外包纱，所述外包纱为金属扁丝，所述金属扁丝横截面的长宽比为30，所述芯纱为芳纶纤维纱。3.根据权利要求2所述的一种新型防刺防割服装面料，其特征在于，所述金属扁丝横截面的长边为300～600μm，所述金属扁丝横截面的短边为10～20μm。4.根据权利...