A rapid method for measuring the quenching uniformity of steel plate is introduced. The technological steps include grinding and polishing small surface area of the surface. Then, the hardness tester is applied to the hardness area of the polishing small area, the hardness value of the small area is chosen, and the hardness uniformity of the steel plate is evaluated. The principle of invention is: the surface hardness and strength of steel plate are related to the uniformity of quenching. The hardness is low, and the volume of quenching water is less. Compared with the traditional method, the invention has the following advantages: it does not destroy the steel plate; it has high efficiency, high accuracy, simple method and strong operability.
【技术实现步骤摘要】
一种快速测量钢板淬火均匀性的方法
本专利技术属于材料热处理
，特别是一种测量淬火钢板性能均匀性的方法。
技术介绍
调质作为一种热处理工艺广泛应用于高强钢等钢板制造领域，钢厂调质生产线一般都采用淬火机，有专用辊道、分区供水冷却等保证钢板力学性能均匀，并使之具有良好的板形。目前检验调质钢板的性能均匀性主要通过在不同位置取样检测力学性能来确认钢板整板性能是否均匀。但这种方法的缺点在于：要通过取样、制样、检测等环节，不仅效率低，而且要破坏钢板。同时这种传统方法耗时长，从而不能迅速检测出结果以指导现场生产。
技术实现思路
本专利技术旨在提供一种克服上述已有技术不足之处的快速测量钢板淬火均匀性的方法，确认调质设备是否满足生产要求。本专利技术的技术方案：一种快速测量钢板淬火均匀性的方法，工艺步骤包括：（1）砂轮机打磨抛光表面小区域：抽取一块进行完淬火热处理的钢板，在钢板头、中、尾部的左、中、右选取九个小区域，使用砂轮机进行打磨和抛光，磨掉表面氧化铁皮，磨面平整光滑，打磨面积不小于100mmX100mm，打磨深度0.3~0.5mm，抛光区域平整光滑；（2）便携式硬度计对抛光小区...
【技术保护点】
一种快速测量钢板淬火均匀性的方法，其特征在于工艺步骤包括：（1）砂轮机打磨抛光表面小区域：抽取一块进行完淬火热处理的钢板，在钢板头、中、尾部的左、中、右选取九个小区域，使用砂轮机进行打磨和抛光，磨掉表面氧化铁皮，磨面平整光滑，打磨面积不小于100mmX100mm，打磨深度0.3~0.5mm，抛光区域平整光滑；（2）便携式硬度计对抛光小区域打硬度：打硬度前用标准试块校准硬度计，打硬度时硬度计垂直于钢板的接触面，摁下按钮，停留2秒后读取数值，每一小区域打9个点；（3）小区域硬度数值取舍：对每一小区域打点测试的九个硬度值，去掉三个最小值和一个最大值，剩余点取平均值；（4）钢板硬度...
【技术特征摘要】
1.一种快速测量钢板淬火均匀性的方法，其特征在于工艺步骤包括：（1）砂轮机打磨抛光表面小区域：抽取一块进行完淬火热处理的钢板，在钢板头、中、尾部的左、中、右选取九个小区域，使用砂轮机进行打磨和抛光，磨掉表面氧化铁皮，磨面平整光滑，打磨面积不小于100mmX100mm，打磨深度0.3~0.5mm，抛光区域平整光滑；（2）便...
【专利技术属性】
技术研发人员：龚立国，周光杰，张勇伟，杨艳，
申请(专利权)人：湖南华菱湘潭钢铁有限公司，
类型：发明
国别省市：湖南,43