本发明专利技术涉及一种特种硅橡胶配方，具体的说是一种高阻燃高瓷化陶瓷化硅橡胶配方，其组份按重量比配比为：甲基乙烯基硅橡胶110‑2为100份，白炭黑为40—65份，羟基硅油为0.05—0.09份，硅藻土为50—150份，石英粉为50—100份，氢氧化铝/氢氧化镁(1/9—6/4)为40—60份，云母粉为20—30份。本发明专利技术的一种高阻燃高瓷化陶瓷化硅橡胶配方，该配方制成的硅橡胶具有高阻燃性，氧指数高达55，高阻燃高瓷化陶瓷化硅橡胶燃烧后烧结成壳体硬度很硬，敲击有金属声；环保无毒。

A high flame retardant and highly porcelain ceramic silicone rubber formula

The invention relates to a special silicone rubber formulation, in particular to a high flame retardant high porcelain ceramic silicone rubber formulation, the components by weight ratio: the ratio of methyl vinyl silicone rubber 110 2 to 100 copies, silica was 40 - 65, 0.05 - 0.09 hydroxy silicone oil. 50 - 150 diatomite, quartz powder is 50 - 100, aluminum hydroxide / magnesium hydroxide (1/9 - 6/4) for 40 - 60, 20 - 30 mica powder. The invention has a high flame retardant, high ceramic and ceramic silicone rubber formula, and the silicone rubber made of the formula has high flame retardance and high oxygen index. The high flame retardant and high ceramic ceramic silicone rubber is sintered into shell after firing, and the hardness is very hard. The knocking has metal sound, and the environment is non-toxic. 55.

【技术实现步骤摘要】
一种高阻燃高瓷化陶瓷化硅橡胶配方
本专利技术涉及一种特种橡胶配方，具体的说是一种高阻燃高瓷化陶瓷化硅橡胶配方。
技术介绍
近年来，随着人们的安全意识的不断加强，国内外对电线电缆的防火耐火等级的要求也进一步提高。为达到防火耐火等级标准的要求，国内外研发了各种不同结构和材料的耐火电线电缆。如：云母带耐火电缆、氧化镁矿物绝缘电缆(MI电缆)、柔性防火电缆、防火泥无机矿物防火耐火电缆。从2005年开始又研发了陶瓷化耐火硅橡胶作绝缘耐火层，通过几年来的实际应用，尽管陶瓷化耐火硅橡胶在很多方面不同程度的解决了上述几种防火耐火电缆材料存在的缺陷和问题，但是防火耐火等级更高的电缆，目前的陶瓷化耐火硅橡胶难以实现，现有技术阻燃性不高，氧指数不到35，壳体硬度不足。本专利技术的一种高阻燃高瓷化陶瓷化硅橡胶配方，该配方制成的硅橡胶具有高阻燃性，氧指数高达55，高阻燃高瓷化陶瓷化硅橡胶燃烧后烧结成壳体硬度很硬，敲击有金属声；环保无毒，符合欧盟ROHS和REACH要求。
技术实现思路
针对现有技术中的问题，本专利技术的一种高阻燃高瓷化陶瓷化硅橡胶配方，该配方制成的硅橡胶具有高阻燃性，氧指数高达55，高阻燃高瓷化陶本文档来自技高网...

【技术保护点】
一种高阻燃高瓷化陶瓷化硅橡胶配方，其特征在于，其组份按重量比配比为：甲基乙烯基硅橡胶110‑2为100份，白炭黑为40—65份，羟基硅油为0.05—0.09份，硅藻土为50—150份，石英粉为50—100份，氢氧化铝/氢氧化镁(1/9—6/4)为40—60份，云母粉为20—30份。

【技术特征摘要】
1.一种高阻燃高瓷化陶瓷化硅橡胶配方，其特征在于，其组份按重量比配比为：甲基乙烯基硅橡胶110-2为100份，白炭黑为40—65份，羟基硅油为...

【专利技术属性】
技术研发人员：刘江滨，张明初，曹中，
申请(专利权)人：安徽宜德电子有限公司，
类型：发明