The present invention provides an antibacterial automotive interior carpet material and its preparation method comprises the following quality copies of the prepared titanium dioxide powder, 80, 50 nano graphene 2 5 copies, 50 copies of 10 pellets. The preparation method comprises the following steps: (1) the titanium dioxide powder, nano graphene and pellets mixed into the extruder, extruder in working temperature of 150 DEG C and 250 extrusion granulating antibacterial masterbatch; (2) add step in the pellets (1) in the preparation of good antibacterial masterbatch, after mixing in the extruder, the content of antibacterial masterbatch in the mixture of 5 20% and the balance of aggregate, in the extruder temperature of 150 DEG C and 200 extrusion spinning equipment through continuous filaments or short fiber. The automobile upholstery carpet fiber material prepared by the preparation method has the function of antibiosis, and the production process is simple, which is suitable for industrialized production.
【技术实现步骤摘要】
一种抗菌汽车内饰地毯材料及其制备方法
本专利技术属于汽车内饰品
，具体涉及一种抗菌汽车内饰地毯材料及其制备方法。
技术介绍
目前常见的汽车内饰地毯大多直接采用PA(俗称尼龙)、PP(俗称丙纶)、PET(俗称涤纶)纤维材料织造，即尼龙、丙纶、涤纶纤维不经过改性直接织造成汽车内饰用地毯，这些汽车内饰地毯虽然具有防污、吸尘等功能，但长时间使用，由于汽车内通风不好，温度湿度不容易控制，汽车内饰地毯容易滋生霉菌，时间一长就会影响驾驶与乘坐人员的身体健康。
技术实现思路
为解决上述问题，本专利技术的目的在于提供一种抗菌汽车内饰地毯材料及其制备方法，具体的技术方案为：一种抗菌汽车内饰地毯材料，由以下质量份的原料制备而成，二氧化钛粉50-80份、纳米石墨烯2-5份，粒料10-50份。优选的，本专利技术所述的一种抗菌汽车内饰地毯材料，由以下质量份的原料制备而成，二氧化钛粉60份、纳米石墨烯3份，粒料30份。优选的，所述粒料为聚对苯二甲酸乙二醇酯。一种本专利技术所述的抗菌汽车内饰地毯材料的制备方法，包括以下步骤：(1)将二氧化钛粉、纳米石墨烯与粒料混匀后放入挤出机中，在挤出机的工作...
【技术保护点】
一种抗菌汽车内饰地毯材料，其特征在于，由以下质量份的原料制备而成，二氧化钛粉50‑80份、纳米石墨烯2‑5份，粒料10‑50份。
【技术特征摘要】
1.一种抗菌汽车内饰地毯材料，其特征在于，由以下质量份的原料制备而成，二氧化钛粉50-80份、纳米石墨烯2-5份，粒料10-50份。2.根据权利要求1所述的一种抗菌汽车内饰地毯材料，其特征在于，由以下质量份的原料制备而成，二氧化钛粉60份、纳米石墨烯3份，粒料30份。3.根据权利要求1或2所述的一种抗菌汽车内饰地毯材料，其特征在于，所述粒料为聚对苯二甲酸乙二醇酯。4.一种权利要求1所...
【专利技术属性】
技术研发人员：李云秀，
申请(专利权)人：华信博伟安徽车辆部件有限公司，
类型：发明
国别省市：安徽,34