The invention relates to a rust removing method for roller surface. It is characterized by the following steps: soaking 20min in 80 degrees with NaOH aqueous solution, wiping the cold roll surface of 10min with HCl water solution, and wiping the cold roll surface with solvent degreasing agent at last. The present invention by three steps, first soaked in alkali solution, and then wipe in weak acid corrosion of roll surface to remove the rust, the solvent degreasing agent to remove rust wipe roll, roll surface residual iron powder, dirt, grease, can quickly and effectively remove rust and corrosion, improve the service life of the roll and cold rolled strip surface quality.
【技术实现步骤摘要】
一种轧辊表面的除锈方法
本专利技术涉及一种轧辊表面的除锈方法。
技术介绍
在冷轧薄板生产线中，如果钢卷出清洗段或者退火炉水淬槽后，带钢表面带水容易造成后续工序辊面出现批量锈蚀问题，该问题严重影响了冷轧薄板生产线的生产节奏，并对生产线生产扣FC、FD等高级别表面产品造成一定的负面影响，最终制约了冷轧厂的产品结构调整。目前国内外各大冷轧厂并无较好的方法根治辊面锈蚀问题，多数企业采取定期更换新辊的临时控制措施，由于更换新辊，需要生产线停车、停产处理，具有消耗成本高、停车处理工序繁琐、备件订货周期长、辊面锈蚀不能根除等诸多缺点。
技术实现思路
针对现有技术中存在的问题，本专利技术的目的在于提供一种轧辊表面的除锈方法的技术方案。所述的一种轧辊表面的除锈方法，其特征在于包括以下步骤：用NaOH水溶液在80度浸泡20min，再用HCl水溶液擦拭锈蚀冷轧辊辊面约10min，最后使用溶剂型脱脂剂擦拭锈蚀冷轧辊辊面。所述的一种轧辊表面的除锈方法，其特征在于所述NaOH水溶液的浓度为5％。所述的一种轧辊表面的除锈方法，其特征在于所述HCl水溶液的浓度为10％。所述的一种轧辊表面的除锈方法，其特征在于所述溶剂型脱脂剂为达赛特。本专利技术通过三个工序，先在碱溶液中浸泡、再用弱酸擦拭锈蚀辊面除去铁锈，最后采用溶剂型脱脂剂擦拭锈蚀辊面，除去辊面残留的铁粉、污垢、油污等，能快速有效清除锈蚀辊面，提高锈蚀辊的使用寿命以及冷轧带材的表面质量。具体实施方式实施例一种轧辊表面的除锈方法，包括以下步骤：用5％NaOH水溶液在80度浸泡20min，再用10％HCl水溶液擦拭锈蚀冷轧辊辊面约10min，最...
【技术保护点】
一种轧辊表面的除锈方法，其特征在于包括以下步骤：用NaOH水溶液在80度浸泡20min，再用HCl水溶液擦拭锈蚀冷轧辊辊面约10min，最后使用溶剂型脱脂剂擦拭锈蚀冷轧辊辊面。
【技术特征摘要】
1.一种轧辊表面的除锈方法，其特征在于包括以下步骤：用NaOH水溶液在80度浸泡20min，再用HCl水溶液擦拭锈蚀冷轧辊辊面约10min，最后使用溶剂型脱脂剂擦拭锈蚀冷轧辊辊面。2.根据权利要求1所述的一种轧辊表面的除锈...
【专利技术属性】
技术研发人员：沈祥红，
申请(专利权)人：江苏锦航机械制造有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。