The invention provides a metal oil removing rust removing agent, which is composed of phosphoric acid, tartaric acid, sodium hydrogen phosphate, thiourea, emulsifier, sodium phosphate, catechol, twelve alkyl sodium sulfonate, accelerant and oxalic acid. The content of each component according to the weight: 12-17 portions of phosphoric acid and tartaric acid 0.02-0.06, sodium hydrogen phosphate 0.1-0.3, thiourea 0.02-0.06 parts, emulsifier 0.3-0.8, sodium phosphate 0.1-0.3, catechol 0.05-0.15, twelve sodium dodecyl sulfate 0.1-0.5, accelerator 0.1-0.5, oxalic acid 0.05-0.15, water 150-200. The invention of the metal oil and rust removing agent, simple process, safety and environmental protection of metal surface rust removal can be carried out at the same time,, zero emissions, no waste residue, no pollution, environmental stability, simple preparation process.
【技术实现步骤摘要】
本专利技术涉及一种金属除油除锈剂,尤其是一种化学法金属材料除油除锈剂。
技术介绍
除油除锈处理是金属表面涂饰前的基本工序。除锈方法大致可分为机械、化学和电化学法三大类,它们各具其特点,适用于不同场合。其中,化学法具有效果好、效率高、工艺操作简单、成本低等一系列优点,所以在工业上获得了广泛应用。但传统的酸液处理方法也存在着明显的缺陷:即处理过程中大量氢气的产生会使金属产生氢脆现象,影响金属本身的强度;同时易形成酸雾,影响操作人员的健康和腐蚀周围的设备及环境。现有的除油除锈液普遍存在着效果差、除锈时间长的缺点,还需要分两道工序分别进行除油、除锈。另外,由于在对钢铁等金属材料进行表面加工时,还需要将表面进行除油的处理步骤,这一步骤通常是在化学除锈之前,这会使得金属表面处理的工艺步骤增加,加大了过程的复杂性,升高了成本,也会造成更多的污染;另外,为达到国家规定的排放标准,传统的处理方法,还需要对废液进行净化才能排放,以及传统的处理方法,需要多工序,人力资源就要加大,这些都增加了企业或者工厂的成本,不利于经济发展、污染环境。
技术实现思路
根据现有技术的不足,本专利技术提供一种金属除油除锈剂,来解决现有除油除锈剂工序繁杂、对环境污染、对工人的身体有害等问题。一种金属除油除锈剂,由磷酸、酒石酸、磷酸氢钠、硫脲、乳化剂、磷酸钠、邻苯二酚、十二烷基磺酸钠、促进剂、草酸、水组成。进一步的,所述各组分含量按照重量份为:磷酸12- ...
【技术保护点】
一种金属除油除锈剂,由磷酸、酒石酸、磷酸氢钠、硫脲、乳化剂、磷酸钠、邻苯二酚、十二烷基磺酸钠、促进剂、草酸组成,所述各组分含量按照重量份为:磷酸12‑17份、酒石酸0.02‑0.06份、磷酸氢钠0.1‑0.3份、硫脲0.02‑0.06份、乳化剂0.3‑0.8份、磷酸钠0.1‑0.3份、邻苯二酚0.05‑0.15份、十二烷基磺酸钠0.1‑0.5份、促进剂0.1‑0.5份、草酸0.05‑0.15份,水150‑200份。
【技术特征摘要】
1.一种金属除油除锈剂,由磷酸、酒石酸、磷酸氢钠、硫脲、乳化剂、磷酸钠、邻苯二酚、
十二烷基磺酸钠、促进剂、草酸组成,所述各组分含量按照重量份为:磷酸12-17份、酒石酸
0.02-0.06份、磷酸氢钠0.1-0.3份、硫脲0.02-0.06份、乳化剂0.3-0.8份、磷酸钠0.1-0.3
份、邻苯二酚0.05-0.15份、十二烷基磺酸钠0.1-0.5份、促进剂0.1-0.5份、草酸0.05-0.15
份,水150-200份。