The invention discloses a heat resistant rubber, the weight of raw material: butyl rubber: 80 ~ 120; sulfur 1 ~ 2; accelerator M0.3 - 0.5; 0.8 accelerator TT - 1.2; Zinc Oxide 3 - 5; Magnesium Oxide 3 - 5; stearic acid 0.8 - 1.2; paraffin 2 to 4; the thermal aging agent D from 1 to 1.3; 50 to 80 parts of aluminum silicate; calcium carbonate from 40 to 60; two of benzene amine antioxidant 1 ~ 3. The invention has the advantages that: through in the formula to increase to a certain percentage of the thermal aging of rubber additives, so as to improve the thermal performance of oxygen free atomic absorption at high temperature, avoid heat free oxygen atoms and the rubber backbone contact and react to the existing heat resistant rubber rubber has a significant improvement in thermal stability relative to the extended rubber product life.
【技术实现步骤摘要】
一种耐热型橡胶
本专利技术涉及一种橡胶材料，特别涉及一种耐热型橡胶。
技术介绍
目前，橡胶管在各领域均有广泛应用，而现有市场上的橡胶管的耐热性能普遍不佳，在高温下使用容易导致过早老化，表面发裂发粘等问题，长时间表面出现掉块从而失去功能，导致耐热橡胶管废弃。
技术实现思路
本专利技术要解决的技术问题是提供一种具有良好耐热性能的耐热型橡胶。为解决上述技术问题，本专利技术的技术方案为：一种耐热型橡胶，其创新点在于：采用如下重量份的原料：丁基橡胶：80～120份；硫磺1～2份；促进剂M0.3～0.5份；促进剂TT0.8～1.2份；氧化锌3～5份；氧化镁3～5份；硬脂酸0.8～1.2份；石蜡2～4份；防热老化剂D1～1.3份；硅酸铝50～80份；碳酸钙40～60份；对苯二胺防老剂1～3份。进一步的，所述的丁基橡胶：80份；硫磺1份；促进剂M0.3份；促进剂TT0.8份；氧化锌3份；氧化镁3份；硬脂酸0.8份；石蜡2份；防热老化剂D1份；硅酸铝50份；碳酸钙40份；对苯二胺防老剂1份。本专利技术的优点在于：通过在配方中以一定的比例增加防热老化助剂，从而提高橡胶中在高温下吸收热氧自...
【技术保护点】
一种耐热型橡胶，其特征在于：采用如下重量份的原料：丁基橡胶：80 ～ 120 份；硫磺 1 ～ 2 份；促进剂M 0.3 ～ 0.5 份；促进剂TT 0.8 ～ 1.2份；氧化锌 3 ～ 5 份；氧化镁 3 ～ 5 份；硬脂酸 0.8 ～ 1.2 份；石蜡 2 ～ 4 份；防热老化剂D 1 ～ 1.3 份；硅酸铝 50 ～ 80 份；碳酸钙40 ～ 60 份；对苯二胺防老剂1 ～ 3 份。
【技术特征摘要】
1.一种耐热型橡胶，其特征在于：采用如下重量份的原料：丁基橡胶：80～120份；硫磺1～2份；促进剂M0.3～0.5份；促进剂TT0.8～1.2份；氧化锌3～5份；氧化镁3～5份；硬脂酸0.8～1.2份；石蜡2～4份；防热老化剂D1～1.3份；硅酸铝50～80份；碳酸钙40...
【专利技术属性】
技术研发人员：徐冬冬，
申请(专利权)人：江苏菲勒电气有限公司，
类型：发明
国别省市：江苏,32