The invention relates to a polyether amide elastomer material and its preparation method of polyether amide elastomer material by long carbon chain nylon, polyether and branched agent copolymerized, which according to the mass percentage: 85 to 15% polyether; long carbon chain nylon 15 85%, branching agent content of polyether and long the total mass of carbon chain nylon 0.05~0.1%, long carbon chain nylon AABB polyamide. Two steps synthesis was used in the preparation. The preparation method is simple and the steps are easy to operate. The prepared polyether amide elastomer material has good melting and molding property, good flexibility and elasticity, high viscosity and melt strength, and can be widely used in the field of foaming molding.
【技术实现步骤摘要】
一种聚醚酰胺弹性体材料及其制备方法
本专利技术涉及一种聚醚酰胺弹性体材料及其制备方法，属于聚合物制备
技术介绍
聚醚酰胺类热塑性弹性体是一种嵌段共聚物，是由高熔点的结晶性聚酰胺硬段和非结晶性或者无定形聚酯或聚醚软段组成。它们的化学组成、片段长度和之间的比例决定了该类材料的物理和化学性质。聚酰胺弹性体强度高、韧性高、弹性好、比重低、耐弯曲疲劳性能好、耐磨性能好、低温性能好，可以广泛地应用于汽车、运动用品、医疗用品、密封件、机械零部件等方面。但是聚醚酰胺弹性体熔融后粘度较低，熔体强度差，发泡成型困难，使得其在聚合物泡沫领域的应用受到很大的限制，有必要对其进行改进。
技术实现思路
本专利技术的目的是为了解决上述问题，提供了一种聚醚酰胺弹性体材料及其制备方法，制备方法简单，步骤易于操作，制备得到的聚醚酰胺弹性体材料能够用于泡沫领域。本专利技术采用如下技术方案：一种聚醚酰胺弹性体材料，其特征在于：所述聚醚酰胺弹性体材料由长碳链尼龙、聚醚和支化剂共聚而成，其中按质量百分数计为：聚醚85-15％；长碳链尼龙15-85％，支化剂的含量占聚醚和长碳链尼龙总质量的0.05～5％...
【技术保护点】
一种聚醚酰胺弹性体材料，其特征在于：所述聚醚酰胺弹性体材料由长碳链尼龙、聚醚和支化剂共聚而成，其中按质量百分数计为：聚醚85‑15%；长碳链尼龙15‑85%，支化剂的含量占聚醚和长碳链尼龙总质量的0.05 ~ 5 %，所述长碳链尼龙为AABB型聚酰胺。
【技术特征摘要】
1.一种聚醚酰胺弹性体材料，其特征在于：所述聚醚酰胺弹性体材料由长碳链尼龙、聚醚和支化剂共聚而成，其中按质量百分数计为：聚醚85-15%；长碳链尼龙15-85%，支化剂的含量占聚醚和长碳链尼龙总质量的0.05~5%，所述长碳链尼龙为AABB型聚酰胺。2.如权利要求1所述的聚醚酰胺弹性体材料，其特征在于：所述AABB型聚酰胺是由二羧酸和二胺聚合而成的，所述二羧酸是碳数6~20的α,ω-直链脂肪族二羧酸，所述二胺是碳数6~20的α,ω-直链脂肪族二胺。3.如权利要求1所述的聚醚酰胺弹性体材料，其特征在于：所述聚醚的分子量为200~3000g/mol的羟基封端的聚醚或氨基封端的聚醚。4.如权利要求1所述的聚醚酰胺弹性体材料，其特征在于：所述支化剂为多元醇或多元酸。5.如权利要求1所述的聚醚酰胺弹性体材料，其特征在于：所述聚醚酰胺弹性体的相对粘度为3.0~3.6，熔体强度为28-32c...
【专利技术属性】
技术研发人员：沈俊毅，陈尚标，胡瑞莉，殷炼伟，
申请(专利权)人：无锡殷达尼龙有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。