一种可功能化的高分子材料及其制备方法技术
A kind of functional polymer material and its preparation method
The invention provides a functional polymer material and a preparation method thereof. The preparation method of the functional polymer material, which is characterized in that the type will include: (L) Delta lactone is shown as monomer, in the absence of solvent, catalyst or catalyst free conditions in the atmosphere is heated to a certain temperature for a period of time, direct implementation the bulk polymerization of the monomers can be functionalized polymer materials. In the solvent-free, non catalyst and cheap gas atmosphere, the product can be polymerized with high molecular weight only when heated, and the obtained polymer product has great functional potential. The invention has the advantages of low cost, low toxicity, high yield, high molecular weight of the polymer product, and high polymer product can be functionalized.
【技术实现步骤摘要】
一种可功能化的高分子材料及其制备方法
本专利技术涉及一种基于CO2/二烯烃的可功能化的高分子材料的制备方法。
技术介绍
二氧化碳因其来源广泛、易得、可再生以及无毒等特点，是目前最具吸引力的C1化工原料。目前，基于二氧化碳的产品大多集中在小分子化合物领域，而在高分子材料领域的案例研究甚少，二氧化碳和环氧树脂通过C-O键的形成而发展出来的聚碳酸酯是目前唯一被工业化的二氧化碳基高分子材料。传统的“六大合成塑料”多是基于聚烯烃的主链为C-C键的高分子化合物，而二氧化碳与环氧树脂制备聚碳酸酯这一过程并无C-C键形成，并未真正实现二氧化碳的还原。因此，发展二氧化碳和烯烃的高分子共聚物是可持续高分子工业发展的一个重大的挑战。尽管长期以来，人们在探究CO2与烯烃直接聚合合成高分子共聚物方面做了很多努力，尝试了二烯烃、乙烯基酯类、丙烯腈等单体，但得到的产物多为分子量较低的寡聚物，一直未实现烯烃与二氧化碳的直接共聚。1976年，Inoue等人首次将二氧化碳与丁二烯采用催化偶联的方法合成得到一种五元环的内酯产物(2-ethylidenehept-5-en-4-olide)。随后，Mus...
【技术保护点】
一种可功能化的高分子材料，其特征在于，其结构式为：
【技术特征摘要】
1.一种可功能化的高分子材料，其特征在于，其结构式为：2.如权利要求1所述的可功能化的高分子材料，其特征在于，所述的基于CO2/二烯烃的可功能化的高分子材料的分子量为5x104～28x104g/mol。3.权利要求1或2所述的可功能化的高分子材料的制备方法，其特征在于，包括：将式(L)所示的δ-内酯作为聚合单体，在无溶剂、无添加剂、催化剂存在或无催化剂的条件下，直接在某种气氛中加热至一定温度反应一段时间，实现该单体的本体聚合得到可功能化的高分子材料。4.如权利要求3所述的可功能化的高分子材料的制备方法，其特征在于，所述的δ-内酯通过钯金属催化的二氧化碳与二烯烃偶联反应得到。5.如权利要求3所述的可功能化的高分子材料的制备方法，其特征在...
【专利技术属性】
技术研发人员：林柏霖，刘慕华，孙运彦，梁源绮，
申请(专利权)人：上海科技大学，
类型：发明
国别省市：上海,31