The present invention relates to a novel poly (caprolactone) shape memory polymer material and its preparation method. The polycaprolactone shape memory polymer material described in the present invention comprises the following components: a stoichiometric monomer of caprolactone and a curing agent. It can also include the following components: curing accelerator, the amount of curing accelerator is 0~2% of the total quality of caprolactone monomer and curing agent. Compared with the existing shape memory materials of the invention has the advantages and beneficial effects: (1) the thermal response of the temperature can be adjusted by adjusting the caprolactone monomer, side chain substituted chain can also be adjusted by the choice of curing agent for regulating; (2) the thermal response time is short, the shape recovery rate; (3) can achieve saturation shape memory effect; (4) convenient preparation, clear structure.
【技术实现步骤摘要】
一种聚己内酯形状记忆高分子材料及其制备方法
本专利技术属于形状记忆材料
，具体涉及一种聚己内酯形状记忆高分子材料及其制备方法。
技术介绍
形状记忆是指具有初始形状的制品，经形变固定之后，通过加热等外部条件刺激手段的处理，又可使其恢复初始形状的现象。自20世纪60年代起，形状记忆材料以其独特的性能引起世界的广泛关注，相关研究也得以迅过发展。形状记忆材料包括形状记忆合金（SMA），形状记忆陶瓷（SMC）和形状记忆高分子(SMP)等。与SMA相比，SMP不仅形变量大、赋形容易、形状响应温度便于调整，而且具有保温、绝缘性能好、不锈蚀、易着色、可印刷、质轻价廉等特点。但其缺点是响应速度慢，形变恢复力小、耐高温性和耐疲劳性差、形状回复精度低。在保持形状记忆功能的前提下，充分运用分子设计技术和材料的改性技术，努力提高SMP的综合性能或赋予性能优异的聚合物以形形状忆功功能，从而开发出新型SMP，并拓宽其应用领域，已成为SMP应用研究和理论研究的重要方向。目前文献报道的形状记忆功能高分子材料主要有聚降冰片烯、反式聚异戊二烯、聚氨酯、交联聚烯烃、苯乙烯-丁二烯共聚物等种类，广泛...
【技术保护点】
一种聚己内酯形状记忆高分子材料，其特征在于，包括化学计量比的以下组合的己内酯单体和固化剂：ε‑己内酯和固化剂甲基六氢苯酐、e‑己内酯和固化剂聚醚胺D230、δ‑己内酯和固化剂聚醚胺D230或e‑己内酯和固化剂丁二酸。
【技术特征摘要】
1.一种聚己内酯形状记忆高分子材料，其特征在于，包括化学计量比的以下组合的己内酯单体和固化剂：ε-己内酯和固化剂甲基六氢苯酐、e-己内酯和固化剂聚醚胺D230、δ-己内酯和固化剂聚醚胺D230或e-己内酯和固化剂丁二酸。2.根据权利要求1所述的一种聚己内酯形状记忆高分子材料，其特征在于，还可包括以下组分：固化促进剂，所述固化促过剂的用量是己内酯单体和固化剂总质量的0~2%。3.根据权利要求2所述的一种聚己内酯形状...
【专利技术属性】
技术研发人员：马海清，崔成杰，谢众，
申请(专利权)人：黑龙江鑫达企业集团有限公司，
类型：发明
国别省市：黑龙江,23