The invention discloses a thermal insulating cement, consists of the following components in part by weight: 50 to 70 portions of cement clinker, gypsum 10 ~ 20, 3 ~ 5 gypsum slag, 3 ~ 5, bentonite 5 ~ 8, 6 ~ 12, titanate micro silica powder 5 ~ 8 from 5 to 10, alumina, expanded perlite 6 - 8, 5 - 10, magnesium carbonate, sodium fluorosilicate 4 ~ 6, 6 ~ 12 sepiolite powder and twelve sodium dodecyl sulfate 1 ~ 3 phr, hydroxypropyl methyl cellulose 3 ~ 5. The invention retains the ingredients in common cement clinker, cement composition change accessories, add a low thermal conductivity of fluorogypsum, titanate, sepiolite powder, micro silica, alumina, perlite, thermal insulation effect is prominent, than the general cement more than twice as high, easy to use.
【技术实现步骤摘要】
一种隔热水泥
本专利技术属于建筑材料
，具体涉及一种隔热水泥。
技术介绍
水泥，粉状水硬性无机胶凝材料，加水搅拌后成浆体，能在空气中硬化或者在水中更好的硬化，并能把砂、石等材料牢固地胶结在一起；它作为一种重要的胶凝材料，广泛应用于土木建筑、水利、国防等工程。目前房屋建筑的隔热节能是节省工作中的重中之重。现行办法是在建筑外墙附加一层隔热层(聚苯乙烯泡沫层或隔热涂料)以达到节能目的。其中，采用聚苯乙烯泡沫层的办法虽有相当的隔热效果，但其施工复杂、成本高、且不持久也不易维护。而隔热涂料的办法虽然施工简单、成本低，但因其涂层太薄而隔热效果很差。实际上，建筑物所使用的水泥，本身也是一种隔热体，只是它的隔热效果较差，所以特种隔热水泥应运而生。
技术实现思路
本专利技术的目的是提供一种隔热水泥，产品环保，具有很好的隔热效果。为了实现上述目的，本专利技术采用如下技术方案：一种隔热水泥，由以下重量份的组分组成：水泥熟料50～70份，氟石膏10～20份，石膏3～5份，矿渣3～5份，膨润土5～8份，钛酸酯6～12份、微硅粉5～8份、氧化铝5～10份、膨胀珍珠岩6～8份、碳酸镁5～10...
【技术保护点】
一种隔热水泥，其特征在于，由以下重量份的组分组成：水泥熟料50～70份，氟石膏10～20份，石膏3～5份，矿渣3～5份，膨润土5～8份，钛酸酯6～12份、微硅粉5～8份、氧化铝5～10份、膨胀珍珠岩6～8份、碳酸镁5～10份、氟硅酸钠4～6份、海泡石粉6～12份、十二烷基硫酸钠1～3份、羟丙基甲基纤维素3～5份。
【技术特征摘要】
1.一种隔热水泥，其特征在于，由以下重量份的组分组成：水泥熟料50～70份，氟石膏10～20份，石膏3～5份，矿渣3～5份，膨润土5～8份，钛酸酯6～12份、微硅粉5～8份、氧化铝5～10份、膨胀珍珠岩6～8份、碳酸镁5～10份、氟硅酸钠4～6份、海泡石粉6～12份、十二烷基硫酸钠1～3份、羟丙基甲基纤维素3～5份。2.根据权利要求1所述的一种隔热水泥，其特征在于，由以下重量份的组分组成：水泥熟料60份，氟石膏15份，石膏4份，矿渣4份，膨润土6份，钛酸酯10份、微硅粉6份、氧化铝8份、膨胀珍珠岩7份、碳酸镁7份、氟硅酸钠5份、海泡石粉10份、十二烷基硫酸钠2份、羟丙基甲基纤维素4份。3.根据权利要求1所述的一种隔热水泥，其特征在...