The invention relates to a cement and production method, belonging to the field of building material technology, and provides a method for producing cement by using casting slag instead of clay and some iron silicon correction raw materials. The casting slag by water quenching, homogenizing, crushing, and crushed limestone sequence by 20 ~ 30 to 70 ~ 80 weight mix proportion of raw materials, raw material grinding, into the ball, calcining clinker in mature material, with 1 ~ 60% casting slag admixture, grinding, preparation of cement products, such as to obtain high strength cement, or without admixture, directly adding retarder made of grinding clinker. By using this kind of waste material instead of clay and correcting raw materials, the cost of cement can be reduced greatly, and the economic benefit is obvious. According to statistics, the cost can be reduced by 20% - 30%.
【技术实现步骤摘要】
一种水泥及生产方法
本专利技术涉及一种水泥及生产方法，属于建筑材料
技术介绍
传统的水泥生产方法是将石灰石、粘土、铁、硅质校正原料按一定比例配料粉磨，煅烧后，再加入混合材或直接利用煅烧后熟料加缓凝剂进行粉磨制成。使用这种方法，要掺与大量粘土和一些校正原料，不但占用农田，还需大量人力、物力来开采和挖取，十分不便。
技术实现思路
本专利技术的目的是要提供一种水泥的生产方法，利用铸造渣代替粘土和一些铁硅校正原料来生产合于国家标准的水泥。技术方案：本专利技术的目的是这样实现的：水泥由石灰石和其它原材料烧制而成，所用的其它原料，主要为铸造渣，当烧制水泥熟料时，使用石灰石与铸造渣的重量配合比，顺序为70~80∶20~30；当制造水泥时，可掺与铸造渣为熟料重量的1~60％进行粉磨，或直接在熟料中加入缓凝剂粉磨制成。由下述工序所组成：1)将出炉的铸造渣，争冷水淬；2)除去较大颗粒，进行均化；3)自然堆放2月左右；4)将破碎的石灰石与破碎的铸造渣按70~80∶20~30的重量比配成生料；5)粉磨、成球、煅烧，制成熟料；6)将熟料加缓凝剂直接粉磨成为水泥，或是在熟料中渗与熟料重...
【技术保护点】
一种水泥，由石灰石和其它原材料烧制而成，其特征在于：所用的其 它原料，主要为铸造渣，当烧制水泥熟料时，使用石灰石与铸造渣的重量配合 比，顺序为70~80∶20~30；当制造水泥时，可掺与铸造渣为熟料重量的1~60％ 进行粉磨，或直接在熟料中加入缓凝剂粉磨制成。
【技术特征摘要】
1.一种水泥，由石灰石和其它原材料烧制而成，其特征在于：所用的其它原料，主要为铸造渣，当烧制水泥熟料时，使用石灰石与铸造渣的重量配合比，顺序为70~80∶20~30；当制造水泥时，可掺与铸造渣为熟料重量的1~60％进行粉磨，或直接在熟料中加入缓凝剂粉磨制成。2.根据权利要求1所述的水泥及生产方法：其特征在于：由...