The invention discloses a method, a preparation of molybdenum disulfide catalyst copper manganate load steps are as follows: 10~15 g ammonium molybdate is added to the 50~100 mL concentration of 1~5 mg/L thioacetamide in ethanol solution, 60 DEG C water bath stirring for 5 to 30 minutes, then add 10~50 mmol and Potassium Permanganate 20~100 cu2cl2 mmol among them, Cu/Mn=1: 2 (molar ratio), adding NaOH solution to pH 8~10, 5~10 h complete precipitation, reaction, filtering to obtain the solid, washing to neutral, drying and calcining at 80, 750 and 2 h, a disulfide catalyst to obtain copper manganate load. The advantages of the present invention are as follows: 1. copper and manganese are mutually combined to form compounds with hetero junction structure; 2. molybdenum disulfide load can help disperse copper manganese and promote each other, so as to improve the degradation rate of pollutants.
【技术实现步骤摘要】
一种二硫化钼负载锰酸铜催化剂的制备方法
本专利技术涉及环境污染控制新材料领域，尤其涉及一种二硫化钼负载锰酸铜催化剂的制备方法。
技术介绍
随着科技的发展，来自工农业生产中产生的毒害有机污染物严重威胁着环境和人类的健康，寻求一种新型高效的环境治理技术具有重要的意义。光催化技术因其节能、高效、污染物降解彻底、无二次污染优点，目前已成为一种具有重要应用前景的新兴环境治理技术。近年来，新型高效的可见光光催化剂的研制成为光催化技术中的一个重要研究内容，其中具有表面等离子共振效应的光催化材料，因其独特的表面物理化学性质和高效的可见光光催化性能，成为研究的热点之一。但纳米颗粒物容易团聚，团聚后表面积大大减小，效果减弱。二硫化钼是一种由钼和硫两种元素组成的化合物，化学式为MoS2。这种化合物属于过渡金属二硫族化合物，它有银黑色光泽，在自然界中以辉钼矿的形式存在，辉钼矿是最常见的含钼元素矿石。二硫化钼晶体通常情况下以粉末形式存在，它不溶于稀酸也不易被氧化。从外表上来看，二硫化钼和石墨很像，以其低摩擦系数和高坚固性常被用作固体润滑剂。块状二硫化钼固体是一种和硅类似的抗磁性间接带隙半导...
【技术保护点】
一种二硫化钼负载锰酸铜催化剂的制备方法，其特征是依次包括如下步骤：将10~15 g钼酸铵加入到50~100 mL浓度为1~5 mg/L的硫代乙酰胺乙醇溶液中，60℃水浴中搅拌5～30分钟，再加入氯化亚铜10~50 mmol和高锰酸钾20~100 mmol，其中Cu/Mn= 1∶2（摩尔比），加入适量NaOH溶液至pH为8~10，沉淀完全，反应5~10 h，过滤得到固体，洗涤至中性，80℃烘干，750℃焙烧2 h，即得到一种二硫化钼负载锰酸铜催化剂。
【技术特征摘要】
1.一种二硫化钼负载锰酸铜催化剂的制备方法，其特征是依次包括如下步骤：将10~15g钼酸铵加入到50~100mL浓度为1~5mg/L的硫代乙酰胺乙醇溶液中，60℃水浴中搅拌5～30分钟，再加入氯化亚铜10~50mmol和...
【专利技术属性】
技术研发人员：程昊，
申请(专利权)人：柳州若思纳米材料科技有限公司，广西科技大学，
类型：发明
国别省市：广西,45