The invention discloses a coal pipe gunning material, components including 3 ~ 5mm bauxite homogenization material 18 ~ 25, 1 ~ 3mm bauxite homogenizing material 10 ~ 15, 1 ~ 0mm silicon carbide 10 ~ 15, 1 ~ 15 ~ 25 0mm of andalusite, not more than 325 orders of brown corundum powder 12 ~ 20, fused calcium aluminate cement 10 ~ 15, 5 ~ 10 alumina powder, Guangxi mud from 5 to 10, carboxymethyl cellulose 2 ~ 3, 0.01 ~ 0.02 explosion-proof fiber. The invention has the advantages of the high quality raw materials of high purity and low impurities, high refractoriness, and through strict control of matrix, in the high temperature formation of mullite phase, mullite phase columnar crystal, the intensity is high, can form mullite structure, so it has high the wear resistance and thermal shock resistance, strong resistance to chemical attack, can save material and reduce the cost for the user, the construction is convenient, can effectively prolong the service life of the whole coal injection pipe, the product has a high price.
【技术实现步骤摘要】
一种喷煤管专用喷补料
本专利技术涉及一种喷煤管专用喷补料，属于耐火材料领域。
技术介绍
现代新型干法水泥生产线，系统设备不断加大，水泥熟料的产量成倍增加，系统内部使用的耐火材料所承受的负荷也越来越大，使用条件越来越苛刻，只有高性能的耐火材料才能保证生产设备的正常运转。喷煤管部位的浇注料承受着高温含尘气流的剧烈冲刷，并且此部位温度变化剧烈，气体中碱蒸气浓度较大，浇注料极易产生开裂、剥落等现象，导致使用寿命严重下降。国内主要水泥企业使用的喷煤管浇注料的寿命波动在6—8个月，无法做到与水泥企业每年1次的大修时间同步。采用浇注料对喷煤管维修，需要经过清理、支模、烘烤等工艺才能投入使用，周期较长，施工劳动强度大，不能满足快速维修的使用要求。采用喷涂的方式对喷煤管进行维护和修补快速、实用，与传统浇注方法比较，经济效益可成倍提高，施工工期短、干燥快(30分钟就硬化)、无需特殊养护，可快速升温，是一种新型的快速施工方式。目前已有的喷涂料多数采用三级高铝矾土或焦宝石作为主体材料，产品体积密度只有2.2g/cm3，在强度、耐磨和抗侵蚀性方面都难以满足喷煤管的使用条件要求，专利CN10...
【技术保护点】
一种喷煤管专用喷补料，其特征在于，成分包括3～5mm矾土均化料18～25份，1～3mm矾土均化料10～15份，1～0mm碳化硅10～15份，1～0mm红柱石15～25份，不大于325目棕刚玉粉12～20份，电熔纯铝酸钙水泥10～15份，氧化铝粉5～10份，广西泥5～10份，羧甲基纤维素2～3份，防爆纤维0.01～0.02份。
【技术特征摘要】
1.一种喷煤管专用喷补料，其特征在于，成分包括3～5mm矾土均化料18～25份，1～3mm矾土均化料10～15份，1～0mm碳化硅10～15份，1～0mm红柱石15～25份，不大于325目棕刚玉粉12～20份，电熔纯铝酸钙水泥10～15份，氧化铝粉5～10份，广西泥5～10份，羧甲基纤维素2～3份，防爆纤维0.01～0....
【专利技术属性】
技术研发人员：朱国平，王立旺，李新明，朱其良，王琪，彭晶晶，
申请(专利权)人：浙江锦诚新材料股份有限公司，
类型：发明
国别省市：浙江,33