The invention relates to a CFB boiler water wall high absorption rate, high thermal conductivity of silicon carbide wear-resistant castable material for silicon carbide, two molybdenum silicide, silicon nitride, silicon oxynitride (Si2ON2), silica sol, the strong mixing seal packaging. Pouring material of the invention has high absorption rate, high thermal conductivity and high wear resistance, is conducive to improve the heat transfer efficiency of CFB boiler waterwall, improve energy utilization efficiency, reduce the boiler exhaust gas temperature, reduce coal consumption, achieve rapid heating of water (or steam) and energy saving effect.
【技术实现步骤摘要】
一种具有高吸收率、高热导率的CFB锅炉水冷壁用碳化硅耐磨浇注料
本专利技术涉及一种具有高吸收率、高热导率的CFB锅炉水冷壁用碳化硅耐磨浇注料，属于无机非金属材料学科耐火材料领域。
技术介绍
CFB锅炉因其具有燃料适应性广、燃烧效率高、负荷调节大、可在床内直接脱硫及实现低NOx排放、燃料制备系统简单、易于实现灰渣综合利用等众多优点，在生产用汽、供热、热电联产、电站锅炉中被广泛采用。由于CFB锅炉炉膛水冷壁和旋风分离器水冷壁受到高浓度、高风速的高流化态物料的冲刷，要求材料的耐磨性能好。目前使用的材料多为刚玉碳化硅浇注料，25℃×24h耐磨性为5.0~6.0cm3（GB/T18301方法），耐磨性能有待进一步提高，而其导热系数通常在2.0~5.0W·m-1·K-1（950℃），热量传输效率有待进一步提高，因此，开发高吸热、高导热，高耐磨浇注料，有利于吸收燃料的热量，同时快速加热水冷壁，提高CFB锅炉的热能利用效率。本专利技术是一种具有高吸收率、高热导率的CFB锅炉水冷壁用碳化硅耐磨浇注料，特别适用于CFB锅炉炉膛水冷壁和旋风分离器水冷壁，能提高热传输效率，提高热能的综合...
【技术保护点】
一种具有高吸收率、高热导率的CFB锅炉水冷壁用碳化硅耐磨浇注料，按照质量百分比表示，其原料组成为：粒度7~3mm的碳化硅 25~44%；粒度5~1 mm的碳化硅 12~30%；粒度1~0.088 mm的碳化硅 6~16%；粒度1~0.088 mm的氮化硅 10~18%；二硅化钼 5~10%；硅氧氮 5~9%；硅溶胶 5~7%。
【技术特征摘要】
1.一种具有高吸收率、高热导率的CFB锅炉水冷壁用碳化硅耐磨浇注料，按照质量百分比表示，其原料组成为：粒度7~3mm的碳化硅25~44%；粒度5~1mm的碳化硅12~30%；粒度1~0.088mm的碳化硅6~16%；粒度1~0.088mm的氮化硅10~18%；二硅化钼5~10%；硅氧氮5~9%；硅溶胶5~7%。2.根据权利要求1所述的浇注料，其特征在于，所述的二硅化钼的粒度≤0.088mm。3.根据权利要求1所述的浇注料，其特征在于，所述的硅...
【专利技术属性】
技术研发人员：陈松林，俞小平，袁林，周严敦，胡建辉，俞洪芳，郭良君，邵学军，邵一平，
申请(专利权)人：瑞泰科技股份有限公司，宜兴瑞泰耐火材料工程有限公司，
类型：发明
国别省市：北京,11