The invention provides a steel slag and slag pot separating agent, which comprises a main material and auxiliary materials, each 1kg main material comprises the following components: the weight of 0.5 0.8kg, refractory clay tailings 0.12 0.475kg, carburetant 0.01 0.04kg and 0.005 0.02kg bentonite, supplementary materials including water glass, water and CMC, each 1kg the main materials used are as follows: water glass with 5 10ml, 0.5%CMC 2 and 8ml 1 water 3kg. The present invention has the advantages of low price, good combination with slag pot, easy separation from steel slag, simple use, and only mixing in proportion, and can be evenly coated on the inner wall of the slag pot after mixing evenly.
【技术实现步骤摘要】
一种钢渣与渣盆分离剂
本专利技术涉及炼钢
，特别是一种钢渣与渣盆分离剂。
技术介绍
炼钢中产生的钢渣一般先放置于渣盆内，再通过渣盆倾倒至渣场，倾倒后取回渣盆重复使用。如果渣盆的内壁上不涂覆任何分离剂，倾倒钢渣时钢渣易粘附在渣盆上，与渣盆不易分离，传统技术多通过敲打渣盆实现钢渣与渣盆的分离，敲打渣盆既会损坏渣盆，又容易引起钢渣飞溅，造成安全事故。现有技术采用耐火骨料、抗渣剂、粘结剂、悬浮剂及其他添加剂配制成钢渣分离剂并涂抹于渣盆内壁形成具有一定厚度、与渣盆结合良好、易与钢渣分离的光滑涂层，该光滑涂层具备1750℃以上的耐火、耐高温、抗侵蚀性，倾倒渣盆时钢渣依靠自身重力与该光滑涂层自然分离。但是，该分离剂价格高，采购成本为2000元/吨。如何设计一种价格低廉、与渣盆结合性能良好、易与钢渣分离的钢渣与渣盆分离剂，是目前需要解决的技术问题。
技术实现思路
为解决上述技术问题，本专利技术提出一种价格低廉、与渣盆结合性能良好、易与钢渣分离的钢渣与渣盆分离剂。本专利技术的技术方案是这样实现的：一种钢渣与渣盆分离剂，包括主料与辅料，每1kg主料中包括如下重量的组分：耐火粘土0....
【技术保护点】
一种钢渣与渣盆分离剂，其特征在于，包括主料与辅料，每1kg的所述主料中包括如下重量的组分：耐火粘土0.5‑0.8kg、尾矿砂0.12‑0.475kg、增碳剂0.01‑0.04kg及膨润土0.005‑0.02kg，所述辅料包括水玻璃、CMC和水，每1kg的所述主料配合如下辅料使用：水玻璃5‑10ml、0.5％CMC 2‑8ml及水1‑3kg。
【技术特征摘要】
1.一种钢渣与渣盆分离剂，其特征在于，包括主料与辅料，每1kg的所述主料中包括如下重量的组分：耐火粘土0.5-0.8kg、尾矿砂0.12-0.475kg、增碳剂0.01-0.04kg及膨润土0.005-0.02kg，所述辅料包括水玻璃、CMC和水，每1kg的所述主料配合如下辅料使用：水玻璃5-10ml、0.5％CMC2-8ml及水1-3kg。2.根据权利要求1所述的钢渣与渣盆分离剂，其特征在于，每1kg的所述主料中包括如下重量的组分：耐火粘土0.65kg、尾矿砂0.32kg、增碳剂0.02kg及膨润土0.01kg，所述辅料...
【专利技术属性】
技术研发人员：李大亮，刘树涛，李张华，
申请(专利权)人：山西建龙实业有限公司，
类型：发明
国别省市：山西,14