The present invention relates to a binder for metal powder injection molding. With the binder comprises the following parts by weight of metal powder injection provided by the invention: 50 paraffin forming 95 copies, 1 15 high density polyethylene and stearic acid or stearic acid derivatives 1 10 copies, 10 copies of 1 polyols. The compounding formula of the invention of the binder feedstock, solid powder volume loading up to 50 70%, can effectively control the sintering shrinkage ratio of material and reach 0.2 1% can control the dimension precision of the scope of the material, the repeated use of more than 10 times the number of products, reduce scrap rate, for the cold runner injection molding process can be very useful. To effectively reduce the subsequent processing of raw materials, reduce production cost.
【技术实现步骤摘要】
一种金属粉末注射成形用粘结剂
本专利技术属于金属成型添加剂领域，具体涉及一种金属粉末注射成形用粘结剂。
技术介绍
金属粉末注射成型技术(MIM)是成形小微型和异形复杂零部件的特殊近净成形技术。粉末注射成形技术使用的原材料即喂料是由金属或陶瓷粉末和粘结剂配制而成的在一定温度下具有一定流动性和成形型的混合物。在粉末注射成型的喂料组成中，粘结剂的种类和构成直接影响到密炼、成型、脱脂等工艺，从而影响到烧结制品的致密度、微观结构、尺寸精度、力学性能等。因此，粘结剂的配置和添加是粉末注射成型喂料制备的关键核心技术。粉末注射成型过程中，由于注射系统和进胶系统会留存大量的喂料，使得喂料将被重复使用。而粘结剂在注射成型过程中由于高温和注射压力作用，将会降解和热疲劳，降低喂料的流动性和成型性，使注射成型产品产生流纹、边角缺料、密度分布不均匀、变形严重等缺陷，并减少喂料的重复使用次数，增加生产成本，并减少喂料的重复使用次数，增加生产成本。
技术实现思路
本专利技术的目的是为了提供一种降低粘结剂在注射成型过程中的降解和热疲劳、提高产品质量、增加喂料的重复使用次数、降低生产成本的金属粉末注射成...
【技术保护点】
一种金属粉末注射成形用粘结剂，其特征在于：包括如下重量份组份：石蜡50‑95份、高密度聚乙烯1‑15份、硬脂酸或硬脂酸衍生物1‑10份、多元醇1‑10份。
【技术特征摘要】
1.一种金属粉末注射成形用粘结剂，其特征在于：包括如下重量份组份：石蜡50-95份、高密度聚乙烯1-15份、硬脂酸或硬脂酸衍生物1-10份、多元醇1-10份。2.根据权利要求1所述的金属粉末注射成形用粘结剂，其特征在于：包括如下重量份组份：石蜡60-80份、高密度聚乙烯5-10份、硬脂酸或硬脂酸衍生物2-8份、多元醇2-8份。3.根据权利要求1所述的金属粉末注射成形用粘结剂，其特征在于：包括如下重量...
【专利技术属性】
技术研发人员：刘兵，陈慧，敬小龙，朱建勇，