三维连通的碳纳米片网状结构负载锗酸铁纳米材料及制备与应用制造技术

本发明专利技术提供一种三维连通的碳纳米片网状结构负载锗酸铁纳米材料，其特征在于，该材料为粒径均一的锗酸铁纳米点均匀负载在三维连通的超薄碳纳米片上，其中锗酸铁纳米颗粒粒径在5‑10nm，三维连通的碳纳米片厚度为3‑10nm，该材料中锗酸铁与总碳量的质量百分比为：(0.4‑0.7):(0.6‑0.3)。本发明专利技术同时提供此种材料的制备方法与应用。

Preparation and application of three dimensional connected carbon nanosheets network structure supported iron germanate nanomaterials

The invention provides a network structure of carbon nanosheets 3D load germanate iron nano material, which is characterized in that the material is germanium acid iron nano dots of uniform size uniform load in ultra-thin carbon nanosheets 3D on the germanate iron nano particles in 5 10nm, 3D connectivity carbon nano sheet thickness is 3 10nm mass percentage of germanate iron and total amount of carbon in the material are: (0.4 0.7 (0.6): 0.3). The invention also provides the preparation method and application of the material.

【技术实现步骤摘要】
三维连通的碳纳米片网状结构负载锗酸铁纳米材料及制备与应用
本专利技术涉及一种三维连通碳纳米片网状结构负载超细锗酸铁纳米材料及制备与应用，属于锂离子二次电池电极材料领域。
技术介绍
作为一种绿色无污染的二次储能器件，锂离子电池得到了越来越多的关注。与传统的镍镉电池相比，其具有功率密度大，使用寿命长，安全性高等特点。现阶段手机、笔记本电脑、摄像机等移动设备的电源大多采用锂离子电池。随着电动汽车(EV)、智能电网以及便携式可穿戴式器件等要求更高能量的器件的产生，对锂离子电池的技术又产生了更高的要求。目前锂离子电池中应用较广的碳负极材料主要为石墨，其理论容量仅为372mAh/g，低的容量难以满足高功率和能量密度设备的需求，所以，开发具有高放电电压，高容量和更长的寿命的新型锂离子电池是目前所面临的一个重大挑战。最近，锗基双金属氧化物(AGeO3或者A2GeO4，A为过渡金属)由于其独特的储锂机制以及高的理论比容量(>1000mAh/g)被认为是一种理想的代替商用石墨负极的电极材料。在第一次嵌锂之后，锗基双金属氧化物会分解成锗以及氧化锂和第二相金属A共同组成的基体，一方面这一基体可以很好地本文档来自技高网...

【技术保护点】
一种三维连通的碳纳米片网状结构负载锗酸铁纳米材料，其特征在于，该材料为粒径均一的锗酸铁纳米点均匀负载在三维连通的超薄碳纳米片上，其中锗酸铁纳米颗粒粒径在5‑10nm，三维连通的碳纳米片厚度为3‑10nm，该材料中锗酸铁与总碳量的质量百分比为：(0.4‑0.7):(0.6‑0.3)。

【技术特征摘要】
1.一种三维连通的碳纳米片网状结构负载锗酸铁纳米材料，其特征在于，该材料为粒径均一的锗酸铁纳米点均匀负载在三维连通的超薄碳纳米片上，其中锗酸铁纳米颗粒粒径在5-10nm，三维连通的碳纳米片厚度为3-10nm，该材料中锗酸铁与总碳量的质量百分比为：(0.4-0.7):(0.6-0.3)。2.上述结构的三维连通碳纳米片网状结构负载超细锗酸铁纳米材料的制备方法，其特征在于包括以下步骤：(1).以蔗糖、葡萄糖、柠檬酸、柠檬酸铵中的一种或几种混合为碳源，以氧化锗为锗源，氯化亚铁为铁源，以碳源中的碳与锗源、铁源中的锗和铁摩尔比为(50～10):1:2，以锗源中的锗与氯化钠的质量比为(0.01-0.1):1计，将碳源、锗源、铁源和氯化钠加入去...

【专利技术属性】
技术研发人员：何春年，韩金志，赵乃勤，李家俊，师春生，刘恩佐，何芳，马丽颖，李群英，
申请(专利权)人：天津大学，
类型：发明
国别省市：天津,12