The invention provides a tempering treatment method for sliding vane and slide piece of rotary air conditioner compressor, which belongs to the compressor technical field. The utility model solves the problem of high cost of the existing slide plate. The rotary air conditioning compressor vane material by chemical composition (quality) of steel prepared%; C:1.0 ~ 1.2%; Si:0.7 ~ 1.2%; Cr:6.8 ~ 8%; V:1.7 ~ 2.1%; Mo:1.1 ~ 1.6%; W:1.1 ~ 1.6%; Ni = 0.25%; Cu:: = 0.25%; S = 0.03%; P:: = 0.03%; Mn: allow residual content is less than 0.3%; the rest is Fe. M2 high speed steel materials compared with the rotary air conditioning compressor vane, while improving the C, Si and Cr content, but decreased Mo, W and Mn content, the overall calculation of the rotary air conditioning compressor vane material cost down at least 8%.
【技术实现步骤摘要】
旋转式空调压缩机滑片和滑片的回火处理方法
本专利技术属于压缩机
，涉及一种旋转式空调压缩机，特别是一种旋转式空调压缩机滑片。本专利技术属于压缩机
，涉及一种旋转式空调压缩机，特别是一种旋转式空调压缩机滑片的回火处理方法。
技术介绍
滑片是旋转式压缩机中的核心部件之一，传统的滑片采用M2高速钢制成，其综合技术要求为经压缩机寿命试验前后相比，制冷量下降不超过5％，换言之，滑片具有较高的精度、耐磨性以及稳定性要求。中国专利文献记载了多篇关于滑片材料组份的技术方案，如制冷压缩机滑片(公开号CN101629573A)，空调压缩机滑片的制造方法(申请公布号CN102251166A)，旋转压缩机的滑片(申请公布号CN102817848A)，压缩机滑片(申请公布号CN103510021A)、压缩机滑片(申请公布号CN103572174A)和制冷压缩机用滑片(申请公布号CN105839013A)。它们可能均解决了各自所解决的技术问题，如降低成本、提高良品率。家用空调器和旋转式空调压缩机自上世纪九十年代引进后，经过二十多年的发展，空调器和空调压缩机行业进入成熟期，竞争进入...
【技术保护点】
一种旋转式空调压缩机滑片，其特征在于，本旋转式空调压缩机滑片的材料由以下化学成分(质量)％组成的钢材制得；C：1.0～1.2％；Si：0.7～1.2％；Cr：6.8～8％；V：1.7～2.1％；Mo：1.1～1.6％；W：1.1～1.6％；Ni：≤0.25％；Cu：≤0.25％；S：≤0.03％；P：≤0.03％；Mn：允许残余含量≤0.3％；余量为Fe和不可避免杂质。
【技术特征摘要】
1.一种旋转式空调压缩机滑片，其特征在于，本旋转式空调压缩机滑片的材料由以下化学成分(质量)％组成的钢材制得；C：1.0～1.2％；Si：0.7～1.2％；Cr：6.8～8％；V：1.7～2.1％；Mo：1.1～1.6％；W：1.1～1.6％；Ni：≤0.25％；Cu：≤0.25％；S：≤0.03％；P：≤0.03％；Mn：允许残余含量≤0.3％；余量为Fe和不可避免杂质。2.一种权利要求1所述旋转式空调压缩机滑片的...