The invention discloses a household decorative sound-absorbing material, as mass fraction, which comprises the following components: 50 concrete 60 copies, 30 copies of 20 modified diatomite ceramic fiber, 10 20 copies, 20 copies, 10 hollow fiber polypropylene fiber 2 5 copies, 5 copies of 10 microporous calcium silicate, 10 Portland cement 20, thickening agent 2 5 copies, 5 copies of accelerator 2 and 80 water 90. The invention also discloses the preparation method of the material. The material in the heating ceramic fiber and hollow fiber, greatly improves the heat degree of material, and copper sulfate by diatomite modified diatomite, increase the porosity, greatly improving the decorative material sound absorption effect, convenient for people to use.
【技术实现步骤摘要】
一种家用吸音装饰材料及其制备方法
本专利技术涉及装饰材料领域，具体是一种家用吸音装饰材料及其制备方法。
技术介绍
装饰材料在家庭装修中使用较为广泛，且装饰材料的分类较多，目前主要分为：室外装饰材料和室内装饰材料，在室内装饰材料中，又可以分为地面装饰材料和墙壁装饰材料，装饰材料在使用该过程中提高了墙壁与地面的美观程度，受到人们的欢迎。但是，由于现在的装饰材料成分简单，装饰材料使用以后，虽然提高了墙壁的美观程度，但是现有的装饰材料不具有吸音功能，导致房屋的隔音效果差，在使用过程中给人们带来一定的不便，影响了人们的居住效果。
技术实现思路
本专利技术的目的在于提供一种家用吸音装饰材料及其制备方法，以解决上述
技术介绍
中提出的问题。为实现上述目的，本专利技术提供如下技术方案：一种家用吸音装饰材料，按质量分数计，包括以下组分：混凝土50-60份、改性硅藻土20-30份、陶瓷纤维10-20份、中空纤维10-20份、聚丙烯纤维2-5份、微孔硅酸钙5-10份、硅酸盐水泥10-20份、增稠剂2-5份、速凝剂2-5份和水80-90份。作为本专利技术进一步的方案：上述家用吸音装饰材料，按质量...
【技术保护点】
一种家用吸音装饰材料，其特征在于，按质量分数计，包括以下组分：混凝土50‑60份、改性硅藻土20‑30份、陶瓷纤维10‑20份、中空纤维10‑20份、聚丙烯纤维2‑5份、微孔硅酸钙5‑10份、硅酸盐水泥10‑20份、增稠剂2‑5份、速凝剂2‑5份和水80‑90份。
【技术特征摘要】
1.一种家用吸音装饰材料，其特征在于，按质量分数计，包括以下组分：混凝土50-60份、改性硅藻土20-30份、陶瓷纤维10-20份、中空纤维10-20份、聚丙烯纤维2-5份、微孔硅酸钙5-10份、硅酸盐水泥10-20份、增稠剂2-5份、速凝剂2-5份和水80-90份。2.根据权利要求1所述的一种家用吸音装饰材料，其特征在于，按质量分数计，包括以下组分：混凝土53-57份、改性硅藻土23-27份、陶瓷纤维13-17份、中空纤维13-17份、聚丙烯纤维3-4份、微孔硅酸钙6-8份、硅酸盐水泥13-17份、增稠剂3-4份、速凝剂3-4份和水84-87份。3.根据权利要求1所述的一种家用吸音装饰材料，其特征在于，按质量分数计，包括以下组分：混凝土55份、改性硅藻土25份、陶瓷纤维15份、中空纤维...