The invention belongs to the field of chemical anti corrosion surface treatment, and specifically relates to the electrostatic powder coating process without chromium passivation zinc plating plate. The technical problem to be solved is to provide a chromium free passivation of galvanized plate electrostatic powder coating process, which comprises the following steps: forming non chromium passivation of galvanized sheet, pre degreasing, degreasing, pottery, washing, drying, electrostatic powder coating, can be cured. The process has the advantages of simple operation and good performance of the obtained plate.
【技术实现步骤摘要】
无铬钝化镀锌板静电粉末涂装工艺
本专利技术属于化学防腐表面处理领域，具体涉及无铬钝化镀锌板静电粉末涂装工艺。
技术介绍
为了防止镀锌板在运输过程中锈蚀，热镀锌板在出厂前都会在镀锌板表面涂敷一层防锈油膜，防止热镀锌钢卷在运输和仓储过程中发生表面腐蚀、生锈等。然而中国家电制造工厂所分布在长江中下游和珠江流域，常年潮湿环境中，涂油镀锌板在运输和仓储过程中不可避免的出现表面锈蚀缺陷，缺陷率在1％以上。无铬钝化镀锌板具有一定的优势，然而无铬钝化镀锌板在冲压成型过程中又会因为冲击压力等出现膜伤等问题，从而影响产品的使用，所以，本专利技术预提供一种无铬钝化镀锌板的涂装工艺。
技术实现思路
本专利技术所要解决的技术问题是针对无铬钝化镀锌板提供一种静电粉末涂装工艺。该工艺以无铬钝化镀锌板为原料，经脱脂、表调、陶化工艺进行静电粉末涂装。从而提供了一种不含RoHS指令中规定的Pb、Cd、Hg、Cr6+、多溴二苯醚PBDE和多溴联苯PBB表面钝化镀锌板，满足国际环保要求；并且涂装后的板具有良好的防腐性能；且该涂装工艺简单、易行，也为镀锌板生产过程中省去了涂油工艺。本专利技术所要解决的技术问题...
【技术保护点】
无铬钝化镀锌板静电粉末涂装工艺，其特征在于：包括以下步骤：将无铬钝化镀锌板冲压成型，经预脱脂、脱脂、陶化、水洗、烘干、静电粉末喷涂，固化即可。
【技术特征摘要】
1.无铬钝化镀锌板静电粉末涂装工艺，其特征在于：包括以下步骤：将无铬钝化镀锌板冲压成型，经预脱脂、脱脂、陶化、水洗、烘干、静电粉末喷涂，固化即可。2.根据权利要求1所述的无铬钝化镀锌板静电粉末涂装工艺，其特征在于：所述无铬钝化镀锌板的钝化层厚度0.8g/m2～1.2g/m2。3.根据权利要求1所述的无铬钝化镀锌板静电粉末涂装工艺，其特征在于：所述预脱脂采用的碱液温度为35～50℃、游离碱度为6～7点。4.根据权利要求1所述的无铬钝化镀锌板静电粉末涂装工艺，其特征在于：所述预脱脂采用的喷淋压力为0.08～0.12Mpa。5.根据权利要求1所述的无铬钝化镀锌板...
【专利技术属性】
技术研发人员：许哲峰，张金波，彭俊，张爱川，彭志刚，
申请(专利权)人：攀钢集团研究院有限公司，
类型：发明
国别省市：四川,51