The invention discloses a method for preparing ethylene glycol antimony, the preparation method comprises the following steps: the weight ratio of 4 ~ 10:1:0.01 ~ 0.05, ethylene glycol antimony oxide and active carbon, from 100 to 150 DEG C, the vacuum degree of 0.09 ~ 0.099MPa 1 ~ 6h after the reaction, the super fine the removal of activated carbon filter, circulating cooling water cooling to 30 ~ 35 degrees of crystallization, centrifugal separation of mother liquid, vacuum vibration bed drying, namely the product of ethylene glycol antimony. The ethylene glycol antimony obtained by the invention overcomes the shortcomings of the existing preparation method that the high-purity antimony oxide three is needed to oxidize two antimony, the production cost is low, and the product whiteness is high.
【技术实现步骤摘要】
乙二醇锑的制备方法
本专利技术属于化工
，更具体地，本专利技术涉及一种新的乙二醇锑的制备方法。
技术介绍
乙二醇锑的外观为白色或青白色结晶颗粒，无毒无气味，遇潮湿空气分解。乙二醇锑是应用于聚酯缩聚反应最为新颖的一种催化剂，它与催化剂三氧化二锑和三醋酸锑相比，具有下列优点：1.在乙二醇溶液中溶解度大，分散性好。2.锑含量高，活性好，可提高聚酯装置生产能力。3.该催化剂本身不会带入新杂质，可使切片提高内在质量，改善后加工可纺性。鉴于以上这些优点，现在越来越多的聚酯生产厂家采用乙二醇锑作为聚酯生产的催化剂。目前，国内的乙二醇锑生产厂家多数是采用三氧化二锑和乙二醇在120-130℃、真空条件下反应制取，但由于温度低，在120-130℃下，乙二醇锑在乙二醇中的溶解度较小，且没有反应精馏塔使溶剂乙二醇回流，导致产量小、能耗高。还有，在纯度要求高的乙二醇锑产品生产时，需要采用纯度较高的三氧化二锑原料，大幅增加了生产成本。
技术实现思路
基于此，为了克服上述现有技术的缺陷，本专利技术提供了一种新的乙二醇锑的制备方法。为了实现上述专利技术目的，本专利技术采取了以下技术方案：一种乙...
【技术保护点】
一种乙二醇锑的制备方法，其特征在于，包括以下步骤：(1)、将重量比为4～10：1：0.01～0.05的乙二醇、氧化锑以及活性炭混合，于100～150℃、真空度0.09～0.099MPa下反应1～6h，反应气相经真空精馏分离；(2)、经超精细过滤器脱除活性炭，用循环冷却水冷却至30～35℃进行结晶；(3)、离心脱除母液后，真空震动床干燥，即得。
【技术特征摘要】
1.一种乙二醇锑的制备方法，其特征在于，包括以下步骤：(1)、将重量比为4～10：1：0.01～0.05的乙二醇、氧化锑以及活性炭混合，于100～150℃、真空度0.09～0.099MPa下反应1～6h，反应气相经真空精馏分离；(2)、经超精细过滤器脱除活性炭，用循环冷却水冷却至30～35℃进行结晶；(3)、离心脱除母液后，真空震动床干燥，即得。2.根据权利要求1所述的乙二醇锑的制备方法，其特征在于，步骤(1)中所述乙二醇、氧化锑以及活性炭的重量比为6～9：1：0.01～0.03。3.根据权利要求2所述的乙二醇锑的制备方法，其特征在于，所述乙二醇、氧化锑以及活性炭的重量比为6～7：1：0.01～0.02。4.根据权利要求1所述的乙二醇锑的制备方法，其特征在于，步骤(1)中所述反...
【专利技术属性】
技术研发人员：邓广兴，陈秀林，易立群，肖飞，
申请(专利权)人：美轲广州化学股份有限公司，
类型：发明
国别省市：广东,44