The invention discloses a method for preparing high performance steel release agent, including the following steps: (1) four methyl two silicone, eight phenyl ring four siloxane, butyl titanate, p-toluenesulfonyl isocyanate, deionized water, heated to 80 DEG C 90, at 60 90min after insulation and spare; (2) to step (1) into the acrylate monomer mixture, addition of initiator, the mixture is heated to 85 DEG C after heat treatment 95, 3 after 4 hours, prepared release agent. The release agent provided by the invention, good stability, good heat resistance, small smoke quantity, lubrication performance in high temperature environment significantly, demoulding effect is good, especially it can effectively isolate carbon migration to the mold surface, greatly prolong the service life of the die.
【技术实现步骤摘要】
一种高性能铸钢用脱模剂的制备方法
本专利技术属于铸钢制备
，具体涉及一种高性能铸钢用脱模剂的制备方法。
技术介绍
铸钢是一种铸造铁合金，是在凝固过程中不经历共晶转变的用于生产铸件的铁基合金的总称。铸钢分为铸造碳钢、铸造低合金钢和铸造特种钢3类。铸钢的优点是有更大的设计灵活性、冶金制造最强的灵活性和可变性、提高整体结构强度和大范围的重量变化。铸钢是铸造合金的一种，以铁、碳为主要元素，含碳量在0-2%之间。由于大部分铸钢中均含有较多的碳元素，其中的碳元素在铸造的过程中，其极易渗透进入模具中，造成模具的强度下降，并且出现变黑的现象，极大地影响了模具的使用寿命。目前市售普通的铸造用脱模剂均不具有隔绝碳元素进入模具中的功能。
技术实现思路
为了解决上述问题，本专利技术提供一种高性能铸钢用脱模剂的制备方法。本专利技术是通过以下技术方案实现的。一种高性能铸钢用脱模剂的制备方法，包括以下操作步骤：（1）按重量份计，将69-75份四甲基二硅氧烷、14-17份八苯基环四硅氧烷、6-10份钛酸丁酯、0.3-0.5份对甲苯磺酰异氰酸酯、30-40份去离子水混合后，加热至80-90℃，保...
【技术保护点】
一种高性能铸钢用脱模剂的制备方法，其特征在于，包括以下操作步骤：（1）按重量份计，将69‑75份四甲基二硅氧烷、14‑17份八苯基环四硅氧烷、6‑10份钛酸丁酯、0.3‑0.5份对甲苯磺酰异氰酸酯、30‑40份去离子水混合后，加热至80‑90℃，保温处理60‑90min后，备用；（2）向步骤（1）所得的混合物中加入其重量0.4‑0.7倍中的丙烯酸酯单体，再向其中加入丙烯酸树脂单体重量0.01‑0.03倍重的引发剂，将混合物加热至85‑95℃后，保温处理3‑4小时后，制得脱模剂。
【技术特征摘要】
1.一种高性能铸钢用脱模剂的制备方法，其特征在于，包括以下操作步骤：（1）按重量份计，将69-75份四甲基二硅氧烷、14-17份八苯基环四硅氧烷、6-10份钛酸丁酯、0.3-0.5份对甲苯磺酰异氰酸酯、30-40份去离子水混合后，加热至80-90℃，保温处理60-90min后，备用；（2）向步骤（1）所得的混合物中加入其重量0.4-0.7倍中的丙烯酸酯单体，再向其中加入丙烯酸树脂单体重量0.01-0.03倍重的引发剂，将混合物加热至85-95℃后，保温处...
【专利技术属性】
技术研发人员：周正明，
申请(专利权)人：合肥正明机械有限公司，
类型：发明
国别省市：安徽,34