The invention relates to a dip coating type scratch resistant polyester fabric fabric, using dip coating on the outer surface of polyester fabric the way to decorate a layer of functional coating, coating the coating slurry function relates to the preparation of the coating agent, silane crosslinking agent and adding pulp tank, mixing evenly, to ammonia pH adjusted to 7.5 ~ 8.5, standing for 2 to 4 hours, and then using the method of dip coating applied to the surface of polyester fabric, drying at 80 DEG C under 0.5 hours, from 120 to 135 DEG C curing environment 1 ~ 1.5 hours, finally under natural conditions in the balance of more than 8 hours. After the surface of polyester fabric is protected by coating material, the fabric has better scratch resistance, and improves the quality of the fabric.
【技术实现步骤摘要】
一种浸渍涂布式耐划伤涤纶织物面料
本专利技术属于涤纶织物面料
，具体涉及一种耐划伤的浸渍涂布的涤纶织物面料。
技术介绍
涤纶是合成纤维中的一个重要品种，是我国聚酯纤维的商品名称。它是以精对苯二甲酸(PTA)或对苯二甲酸二甲酯(DMT)和乙二醇(EG)为原料经酯化或酯交换和缩聚反应而制得的成纤高聚物--聚对苯二甲酸乙二醇酯(PET)，经纺丝和后处理制成的纤维。涤纶织物具有较高的强度与弹性恢复能力，因此，其坚牢耐用、抗皱免烫。涤纶织物吸湿性较差，穿着有闷热感，同时易带静电、沾污灰尘，影响美观和舒适性。不过洗后极易干燥，且湿强几乎不下降，不变形，有良好的洗可穿性能。涤纶是合纤织物中耐热性最好的面料，具有热塑性，可制做百褶裙，褶裥持久。同时，涤纶织物的抗熔性较差，遇着烟灰、火星等易形成孔洞。因此，穿着时应尽量避免烟头、火花等的接触。涤纶织物的耐光性较好，除比腈纶差外，其耐晒能力胜过天然纤维织物。不断开发面料的新功能是涤纶织物面料发展的趋势。
技术实现思路
本专利技术的目的是提供一种耐划伤的浸渍涂布式涤纶织物面料。本专利技术解决上述问题所采用的技术方案为：一种浸渍涂布式耐...
【技术保护点】
一种浸渍涂布式耐划伤涤纶织物面料，其特征在于：是在涤纶基布的外表面采用浸渍涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用浸渍涂布的方式施加到涤纶基布表面，于80℃环境下烘干0.5小时，于120～135℃环境下固化1～1.5小时，最后在自然条件下平衡8小时以上。
【技术特征摘要】
1.一种浸渍涂布式耐划伤涤纶织物面料，其特征在于：是在涤纶基布的外表面采用浸渍涂布的方式装饰一层功能涂层，所述功能涂层所涉及的涂层浆的制备是将涂层胶、硅烷和交联剂加入制浆罐，搅拌均匀后，以氨水调节pH至7.5～8.5范围，静置2～4小时，然后采用浸渍涂布的方式施加到涤纶基布表面，于80℃环境下烘干0.5小时，于120...