The invention relates to a preparation method of a hard alloy comprises the following steps: WC powder, Co powder, rare earth and alkaline earth were dissolved into the liquid dispersion medium, pour into the mixing bucket, and evenly mixed to prepare a mixture; the mixture into the ball mill to 36 40H at 100 DEG C vacuum drying, and then add the slurry mixing and drying, using a sieve sieve made of granular material; material particle molding, vacuum dewaxing at 1200 DEG C, and then 1300 under high temperature sintering, made of hard alloy. The preparation method of hard alloy has the advantages of easy control of crystal grain growth, no need of high temperature assistance, easy oxidation, good performance, low cost, short process and short operation.
【技术实现步骤摘要】
一种硬质合金的制备方法
本专利技术属于复合金属
，涉及一种硬质合金的制备方法。
技术介绍
硬质合金材料作为一种广泛应用的刀具材料和结构材料，具有一系列优良的性能特点：1、硬度高且具有良好的耐磨性和刚性；2、具有很高的弹性模量，常温下刚性好；3、抗压强度高，导热系数大；化学性稳定好，部分硬质合金耐酸碱能力强，高温氧化现象也不明显；4、化学性稳定好，部分硬质合金耐酸碱能力强，高温氧化现象也不明显；5、冲击韧性及热膨胀系数较低；硬质合金的上述特点，使其在耐磨材料、耐高温材料等方面占据了重要的位置。然而在硬质合金的烧结技术中，仍然存在着一些问题：氢气烧结的优点是还原性保护气氛，缺点是残余孔隙；真空烧结的优点是不易氧化，缺点是晶粒生长不易控制，工艺难掌握；微波烧结的优点是烧结快速，性能优良，缺点是成本高；热压烧结的优点是操作简单，规模生产，缺点是制品形状简单，成本高；热等静压烧结的优点是性能优良，均匀，缺点是成本高；低压烧结的优点是性能优，均匀性好，工序短，缺点是成本高；SPS烧结的优点是快速、降低烧结温度，缺点是成本高、处于工艺探索阶段；反应烧结的优点是不变形、少加...
【技术保护点】
一种硬质合金的制备方法，其特征在于，包括步骤：(1)将WC粉体、Co粉体、稀土和碱土分别溶入液相分散介质后，倒入混料桶，并混合均匀制得混合体；(2)将所述混合体放入球磨机球磨36‑40h，在100℃下真空干燥、然后加入料浆搅拌后干燥，用筛子过筛，制成料粒；(3)将料粒压制成型、脱蜡，然后在1200℃‑1300℃的条件下真空烧结，制得硬质合金。
【技术特征摘要】
1.一种硬质合金的制备方法，其特征在于，包括步骤：(1)将WC粉体、Co粉体、稀土和碱土分别溶入液相分散介质后，倒入混料桶，并混合均匀制得混合体；(2)将所述混合体放入球磨机球磨36-40h，在100℃下真空干燥、然后加入料浆搅拌后干燥，用筛子过筛，制成料粒；(3)将料粒压制成型、脱蜡，然后在1200℃-1300℃的条件下真空烧结，制得硬质合金。2.根据权利要求1所述的硬质合金的制备方法，其特征在于，步骤(1)中，所述WC粉体、Co粉体、稀土和碱土的重量比为2：1：0.1：0.1。3.根据权利要求1所述的硬质合金的制备方法，其特征在于，步骤(1)中，所述液相分散介质中还加入抑制剂，所述抑制剂为WC-Co硬质合金，所述Co含量为10wt.％。4.根据权利要求1所述...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。