防粘扣固体润滑涂料及其制备方法和涂覆方法技术

本发明专利技术公开了一种防粘扣固体润滑涂料及其制备方法和涂覆方法，其包括按重量百分数计的如下组分：混合树脂：16～60％；增韧剂：1～5％；固体润滑剂：26～70％；耐腐蚀剂：2～15％；耐磨助剂：1～5％；其余助剂：0.01～0.1％；余量为溶剂。本发明专利技术的优点在于：本发明专利技术的油套管接头表面涂覆方法，能够方便地控制涂层的厚度，工艺简单，操作容易，便于工业化实施。

Anti sticking solid lubricating paint, preparation method and coating method thereof

The invention discloses a preparation method and anti sticking coating method of solid lubricant coating and buckle system, which comprises the following components according to weight percentage points: 16 to 60%: mixed resin; toughening agent: 1 ~ 5%: 26 ~ 70%; solid lubricants; corrosion agent: 2 ~ 15%; wear-resistant additives: 1 ~ 5%: 0.01 ~ 0.1%; other auxiliary solvent. The advantages of the invention are as follows: the coating method of the oil casing joint of the invention can easily control the thickness of the coating, and has the advantages of simple process, easy operation, and convenient for industrialized implementation.

【技术实现步骤摘要】
防粘扣固体润滑涂料及其制备方法和涂覆方法
本专利技术涉及在石油勘探开采中使用的油套管用接头表面处理方法，属于表面处理
，特别涉及一种油套管螺纹接头用固体润滑涂料及涂覆方法。
技术介绍
石油天然气勘探开发必须使用油套管产品，套管用螺纹连接成套管柱，形成采油通道，油管用螺纹连接成油管柱进行采油。油套管接头由内螺纹和外螺纹组成，使用过程通过上扣和卸扣进行螺纹的拧紧和松开，螺纹接头相当于一对摩擦副，当内螺纹和外螺纹表面相互接触时，从微观来看，两个接触体的实际接触面积只在结合表面少数微凸体上，由于接触压力很高，引起微凸体塑性变形，局部形成焊合点，同时由于内螺纹和外螺纹材质相同，互溶性大，在内外螺纹表面的相对滑动时，引起油套管螺纹接触部位金属迁移产生粘着失效，即油套管接头发生粘扣。由于油套管接头重复上卸扣不发生粘扣是其重要性能指标之一，为此，对接头连接表面进行磷化、电镀铜锡合金等表面处理，在上扣时，再采用在接头连接处涂覆螺纹脂，确保接头连接处不发生粘扣失效。但螺纹脂中含有以铅、锌为主的重金属粉末，这些重金属粉末对环境会造成严重污染，不能满足环境保护的要求，目前北海在石油天然气勘探开发中已禁本文档来自技高网...

【技术保护点】
一种防粘扣固体润滑涂料，其特征在于，包括按重量百分数计的如下组分：

【技术特征摘要】
1.一种防粘扣固体润滑涂料，其特征在于，包括按重量百分数计的如下组分：2.如权利要求1所述的防粘扣固体润滑涂料，其特征在于，所述溶剂的用量为固体组分总重量的1～3倍。3.如权利要求1所述的防粘扣固体润滑涂料，其特征在于，所述混合树脂为聚酰胺酰亚胺、环氧树脂和聚乙烯醇缩丁醛的混合物。4.如权利要求3所述的防粘扣固体润滑涂料，其特征在于，所述聚酰胺酰亚胺、环氧树脂和聚乙烯醇缩丁醛的重量比为(10～30)：(5～20)：(1～10)。5.如权利要求1所述的防粘扣固体润滑涂料，其特征在于，所述增韧剂为柠檬酸三正丁酯、邻苯二甲酸二辛脂和乙酰柠檬酸三正丁酯中的至少一种。6.如权利要求1所述的防粘扣固体润滑涂料，其特征在于，所述固体润滑剂为二硫化钼、三氧化二锑和聚四氟乙烯的混合物。7.如权利要求6所述的防粘扣固体润滑涂料，其特征在于，所述...

【专利技术属性】
技术研发人员：王琍，罗蒙，蔡蕴斌，
申请(专利权)人：宝山钢铁股份有限公司，
类型：发明
国别省市：上海,31