The invention belongs to the field of architectural decoration technology, in particular relates to a finishing agent and a preparation method thereof. The invention comprises the following raw materials in parts by weight: 30 to 40 portions of acrylic resin, epoxy resin, 15 to 20 copies of 0.3 ~ 0.5, 10 ~ 12 phr initiator modified filler, 1 ~ 3 and 60 ~ 70 butanone emulsifier; modified packing the graphite and mica comminution after mixed powder, then mixing the powder and slurry mixed fermentation, and then sterilized, centrifuged to obtain precipitate, and the precipitate of zinc nitrate reaction after filtration, get a residue, the residue can be calcined. The finishing agent prepared by the invention has good antibacterial property and good abrasion resistance, and has wide application prospect.
【技术实现步骤摘要】
一种涂饰剂及其制备方法
本专利技术属于建筑装饰
，具体涉及一种涂饰剂及其制备方法。
技术介绍
随着建筑标准的不断提高和混凝土表面不再抹灰工程的逐年增加，建筑行业不仅开始大规模使用模板，而且对模板质量的要求也越来越高。早期建筑工程基本上是直接使用胶合板素板作为模板，但由于素板抗水和耐磨性能差，因此其重复使用次数仅为10～15次，有时甚至更低。为了改变这种状况，改善建筑模板的使用性能，有必要对模板的表面进行处理。CN1386811A公开了一种建筑模板漆，该涂料每吨中含有异氰酸酯230～270kg，二丁酯50～80kg，磷酸0.5～1kg，聚醚33070～100kg，聚醚63520～49kg，二甲苯400～540kg。该涂料具有优异的附着力，硬度，韧性和耐碱、耐热、耐磨性能，还具有优异的脱模性能，适合做木模、竹模的表面处理剂和钢模等各种模具的脱模剂。CN101830032A公开了一种可用于防止或减少混凝土与模板表面相互粘接的混凝土长效脱模剂及其制备方法，脱模剂包括模板漆主剂和附着剂两种制剂，其中模板漆主剂主要由环氧树脂或不饱和聚酯树脂或丙烯酸树脂、溶剂、添加剂通过...
【技术保护点】
一种涂饰剂，其特征在于，包括以下重量份数的原料：30～40份丙烯酸树脂、15～20份环氧树脂、0.3～0.5份引发剂、10～12份改性填料、1～3份乳化剂和60～70份丁酮。
【技术特征摘要】
1.一种涂饰剂，其特征在于，包括以下重量份数的原料：30～40份丙烯酸树脂、15～20份环氧树脂、0.3～0.5份引发剂、10～12份改性填料、1～3份乳化剂和60～70份丁酮。2.根据权利要求1中所述的一种涂饰剂，其特征在于，所述的环氧树脂为环氧树脂E-44、环氧树脂601中的一种或两种。3.根据权利要求1中所述的一种涂饰剂，其特征在于，所述的引发剂为过硫酸钾、过氧化月桂酰、叔丁基过氧化氢中的一种或几种。4.根据权利要求1中所述的一种涂饰剂，其特征在于，所述的改性填料是由以下步骤得到的：（1）将200～300g石墨、100～200g绢云母粉碎后，得到混合粉末，将混合粉末和600～800mL沼液在35～45℃下密封发酵8～10天，得到发酵产...
【专利技术属性】
技术研发人员：方晓俊，宋玲，
申请(专利权)人：常州市日臣艺术装饰材料有限公司，
类型：发明
国别省市：江苏,32