一种改善乙二醇紫外透过率的方法技术
A method for improving UV transmittance of ethylene glycol
The invention discloses an improved glycol UV transmittance method, the method using ethylene glycol solution and hydrogen as raw material, made of metal alloy catalyst; the metal alloy catalysts including nickel, one or more rare earth elements, tin and aluminum; components by weight were 10, 90 1 5 copies, 1 copies of 60 and 5 9. The method of the invention uses cheap, stable alloy in the water phase, without the carrier alloy as the catalyst, to continuously reduce the unsaturated impurities in ethylene glycol. When the method is applied to industrial continuous production, the use of this alloy catalyst is of great importance to the long-term and stable operation of the system and the control of the production cost.
【技术实现步骤摘要】
一种改善乙二醇紫外透过率的方法
本专利技术涉及化工乙二醇生产领域。更具体地，涉及一种去除乙二醇中杂质的方法。
技术介绍
乙二醇作为瓶级聚酯和纤维级聚酯的重要单体，具有很大的应用市场。乙二醇的生产路线包括两种，一种路线是以石油基烯烃或者生物基烯烃为原料，采用氧化和水合法，另一种路线是以草酸酯为原料，采用加氢法。影响乙二醇产品质量的杂质主要来源于乙烯氧化过程中的氧化副产物(如丙烯醛，巴豆醛等)，或者草酸酯加氢过程中产生的酸、醛或者酯类。尤其在催化剂使用中后期，随着反应温度升高，这些副产物的种类和数量会更多。国际上广泛应用产品紫外透光率(UV值)作为一项综合性指标来判别乙二醇产品的质量，通用的方法是测定乙二醇对220nm～350nm波长的紫外透光率来检测乙二醇中杂质的含量。这些杂质会大幅度降低乙二醇在220-350nm的紫外透过率，即紫外透过率反映了乙二醇中杂质的多少。UV值不合格的乙二醇将影响下游的聚酯产品的质量，包括强度，颜色和着色等。影响乙二醇紫外透过率的杂质很难通过精馏的方法除去，通常采用物理法和化学法来去除杂质，其中物理法主要采用吸附和膜分离法，化学法主要采用...
【技术保护点】
一种改善乙二醇紫外透过率的方法，该方法以乙二醇溶液和氢气为原料，其特征在于，该方法采用金属合金催化剂；所述金属合金催化剂包括镍、一种或多种稀土元素、锡和铝；各组分按重量份数计分别为10‑90份、1‑5份、1‑60份和5‑9份。
【技术特征摘要】
1.一种改善乙二醇紫外透过率的方法，该方法以乙二醇溶液和氢气为原料，其特征在于，该方法采用金属合金催化剂；所述金属合金催化剂包括镍、一种或多种稀土元素、锡和铝；各组分按重量份数计分别为10-90份、1-5份、1-60份和5-9份。2.根据权利要求1所述的方法，其特征在于，所述金属合金催化剂包括镍、一种或多种稀土元素、锡、铝和钨；各组分按重量份数计分别为10-90份、1-5份、1-60份、5-9份和1-90份。3.根据权利要求1所述的方法，其特征在于，所述金属合金催化剂包括镍、一种或多种稀土元素、锡、铝、钨和钼，各组分按重量份数计分别为10-90份、1-5份、1-60份、5-9份、1-90份和0.5-20份。4.根据权利要求1所述的方法，其特征在于，所述金属合金催化剂包括镍、一种或多种稀土元素、锡、铝、钨、钼、和硼或磷，各组分按重量份数计分别为10-90份、1-5份、1-60份、5-9份、1-90份、0.5-20份和0.01-5份。5.根据权利要求1所...