The invention discloses a process for manufacturing a bamboo board, which comprises the following steps: step 1: the harvesting of bamboo processing into left bamboo tablets; step 2: the bamboo carbonization treatment, carbonization conditions: temperature 120, 3 high pressure, 70 minutes; 3 steps: Step 2 drying the bamboo is soaked in copper oxide antibacterial agent in 36 minutes; step 4: dry carbonization completed bamboo bamboo glue; step 5:, and toward the same direction according to the blank of bamboo, by heating and pressing forming a layer of blank; the blank is a single step 6: into drying out infiltration after leaching in the blank of tung oil, according to the grain group blank, and through the formation of green bamboo plate pressure. The bamboo green board of the invention has the advantages of simple manufacturing method, high yield and long service life.
【技术实现步骤摘要】
一种竹青板的制造工艺
本专利技术涉及一种竹青板的制造工艺。
技术介绍
现有的竹青板的制造方法复杂，成品率低，使用寿命短。
技术实现思路
本专利技术的目的是克服现有产品中的不足，提供一种竹青板的制造工艺。为了达到上述目的，本专利技术是通过以下技术方案实现的：一种竹青板的制造工艺,包括如下步骤:步骤1:将采伐的竹子处理加工成留青竹片；步骤2:将竹片进行炭化处理,炭化条件为:温度120℃,压力3大气压,时间70分钟；步骤3：将步骤2干燥好的竹片浸泡在氧化铜抗菌剂中36分钟；步骤4:将炭化完成的竹片进行晾干；步骤5:将竹片涂胶,并按竹青朝向同一方向组坯，通过加热加压形成单层毛坯件；步骤6:将单层的毛坯件放入到浸桐油中浸润后取出烘干,再将毛坯件按照顺纹组坯,并通过加压形成竹青板。本专利技术的有益效果如下：竹青板的制造方法简单，成品率高，使用寿命长。具体实施方式下面对本专利技术的技术方案作进一步说明：实施例1：一种竹青板的制造工艺,包括如下步骤:步骤1:将采伐的竹子处理加工成留青竹片；步骤2:将竹片进行炭化处理,炭化条件为:温度120℃,压力3大气压,时间70分钟；步骤3：将步骤...
【技术保护点】
一种竹青板的制造工艺,其特征在于，包括如下步骤:步骤1:将采伐的竹子处理加工成留青竹片；步骤2:将竹片进行炭化处理,炭化条件为:温度120℃,压力3大气压,时间70分钟；步骤3：将步骤2干燥好的竹片浸泡在氧化铜抗菌剂中36分钟；步骤4:将炭化完成的竹片进行晾干；步骤5:将竹片涂胶,并按竹青朝向同一方向组坯，通过加热加压形成单层毛坯件；步骤6:将单层的毛坯件放入到浸桐油中浸润后取出烘干,再将毛坯件按照顺纹组坯,并通过加压形成竹青板。
【技术特征摘要】
1.一种竹青板的制造工艺,其特征在于，包括如下步骤:步骤1:将采伐的竹子处理加工成留青竹片；步骤2:将竹片进行炭化处理,炭化条件为:温度120℃,压力3大气压,时间70分钟；步骤3：将步骤2干燥好的竹片浸泡在氧化铜抗菌...
【专利技术属性】
技术研发人员：李刚，
申请(专利权)人：安吉六合工艺品有限公司，
类型：发明
国别省市：浙江,33