The invention discloses a preparation method for pickling and cleaning head processing, by hydrochloric acid, sulfuric acid, phosphoric acid, Potassium Permanganate, sulfonated lignin inhibitor, acid fog inhibitor, quaternary ammonium cationic gemini surfactant, alkyl benzene sulfonate surfactant, xylitol stabilizer, lauric acid oxidizing agent, methylene two naphthalene sulfonate dispersing agent, ethylene glycol, ethanolamine absorbent, glycerol and distilled water; for the head cleaning processing pickling solution suitable for various head processing in the pickling process, can effectively remove the formed head points on the surface of welding slag, slag, oil and oxide, so as to improve the processing effect of head the.
【技术实现步骤摘要】
一种用于封头清洗加工的酸洗液及其制备方法
本专利技术涉及一种用于封头清洗加工的酸洗液及其制备方法。
技术介绍
目前钢材的清洗工艺主要是酸洗，成分主要有硫酸、盐酸、硝酸、氢氟酸等，依照不同的比例，添加不同的添加剂配制而成。但在实际中，现有的酸洗工艺，存在酸消耗量大，酸雾也大，其废酸排放周期短等缺点。现在的酸洗液倾向于在酸中加入不同的物质以起到稳定酸液、促进清洗、缓释钢材的作用，从而使钢材腐蚀、延长使用时间。关于此类酸洗液添加剂的报道较少。华中科技大学；武汉永兴化工有限责任公司申请专利CN01133516.5介绍了一种钢铁酸洗促进剂。本专利技术公开了一种钢铁酸洗促进剂，其成分及重量配比为无机盐还原剂(如亚硫酸钠、次硫酸钠、一缩二亚硫酸钠、硫代硫酸钠、硫代硫酸铵中的一种或二种)，10％～80％；有机金属离子螯合剂(如葡萄糖酸和盐、酒石酸和盐、柠檬酸和盐、乙二胺四乙酸二钠盐中的一种)，1％～20％；增效剂(如丁炔二醇、乙二醇、丙三醇中的一种)，1％～20％；水10％～50％。本钢铁酸洗促进剂特别适用于添加在酸洗液中促进清洗各种钢铁(尤其是硅钢)带钢和型材表面生成的紧密氧化...
【技术保护点】
一种用于封头清洗加工的酸洗液，其特征在于：由盐酸20‑34份、硫酸27‑35份、磷酸20‑28份、高锰酸钾17‑29份、磺化木质素缓蚀剂6‑8份、氢氟酸抑雾剂7‑13份、季铵盐阳离子型双子表面活性剂5‑9份、直链烷基苯磺酸钠表面活性剂4‑6份、木糖醇稳定剂1‑3份、月桂酸氧化剂1‑3份、亚甲基二萘磺酸钠扩散剂4‑6份、乙二醇溶剂3‑5份、一乙醇胺吸收剂1‑3份、甘油1‑3份和蒸馏水40‑60份制成。
【技术特征摘要】
1.一种用于封头清洗加工的酸洗液，其特征在于：由盐酸20-34份、硫酸27-35份、磷酸20-28份、高锰酸钾17-29份、磺化木质素缓蚀剂6-8份、氢氟酸抑雾剂7-13份、季铵盐阳离子型双子表面活性剂5-9份、直链烷基苯磺酸钠表面活性剂4-6份、木糖醇稳定剂1-3份、月桂酸氧化剂1-3份、亚甲基二萘磺酸钠扩散剂4-6份、乙二醇溶剂3-5份、一乙醇胺吸收剂1-3份、甘油1-3份和蒸馏水40-60份制成。2.如权利要求1所述的一种用于封头清洗加工的酸洗液，其特征在于：由盐酸34份、硫酸27份、磷酸20份、高锰酸钾17份、磺化木质素缓蚀剂6份、氢氟酸抑雾剂7份、季铵盐阳离子型双子表面活性剂5份、直链烷基苯磺酸钠表面活性剂4份、木糖醇稳定剂1份、月桂酸氧化剂1份、亚甲基二萘磺酸钠扩散剂4份、乙二醇溶剂3份、一乙醇胺吸收剂1份、甘...
【专利技术属性】
技术研发人员：叶一舟，萧亚兵，叶明荣，朱士林，
申请(专利权)人：浙江莱德桑机械有限公司，
类型：发明