The invention discloses a cement kiln waste heat power generation high temperature resistant coatings for wear, consists of the following components in part by weight: 50 to 70 portions of cement clinker, gypsum 10 ~ 20, 3 ~ 5 gypsum slag, 3 ~ 5, bentonite 5 ~ 8, 6 ~ 12 titanate from 5 to 8, micro silica, aluminum oxide 5 - 10, 6 - 8, expanded perlite magnesium carbonate from 5 to 10, 4 to 6 parts of sodium fluosilicate, sepiolite powder 6 ~ 12, 1 ~ twelve sodium dodecyl sulfate 3, hydroxypropyl methyl cellulose 3 ~ 5. The invention retains the ingredients in common cement clinker, cement composition change accessories, add a low thermal conductivity of fluorogypsum, titanate, sepiolite powder, micro silica, alumina, perlite, thermal insulation effect is prominent, than the general cement more than twice as high, easy to use.
【技术实现步骤摘要】
一种水泥窑余热发电用耐磨耐高温涂料
本专利技术公开了一种涂料，具体是一种适用于水泥窑余热发电的耐磨耐高温涂料，属于耐热材料
技术介绍
新型干法水泥熟料生产企业中由窑头熟料冷却机和窑尾预热器排出的350℃左右废气，其热能大约为水泥熟料烧成系统热耗量的35％，而新型干法水泥总量的增长对水泥工业用电总量的增长起到了推动作用，一定程度上加剧了电能的供应紧张局面，低温余热发电技术的应用，可将排放到大气中占熟料烧成系统热耗35％的废气余热进行回收利用来节能降耗，因此在水泥业发展余热发电项目是行业及国家经济发展的必然。但水泥窑余热发电的管道设备中的烟气中带着磨损性较强的熟料微粒，该做粒具有粉尘粒径粗、磨损性大等特点，会严重磨损锅炉、降低锅炉的使用寿命，而且余热发电设备中的风管变径多、弯头多、风速快，进而会造成更严重的磨损，但现有的用于余热发电的耐火材料通常只具有较高的耐热性能，而耐磨性能较低。
技术实现思路
本专利技术的目的是提供一种水泥窑余热发电用耐磨耐高温涂料，能够在具有较高的耐热性能的前提下具有较高的耐磨性能，特别适用于水泥窑余热发电。为了实现上述目的，本专利技术采...
【技术保护点】
一种水泥窑余热发电用耐磨耐高温涂料，其特征在于，由以下重量份的组分组成：硅莫砖粉50～70份，氟石膏10～20份，硅灰3～5份，矿渣3～5份，铝酸盐水泥10～20份，高铝细粉10～20份、氧化铝粉5～10份、碳酸镁5～10份、三聚磷酸纳4～6份、十二烷基硫酸钠1～3份、木质素磺酸纳3～5份。
【技术特征摘要】
1.一种水泥窑余热发电用耐磨耐高温涂料，其特征在于，由以下重量份的组分组成：硅莫砖粉50～70份，氟石膏10～20份，硅灰3～5份，矿渣3～5份，铝酸盐水泥10～20份，高铝细粉10～20份、氧化铝粉5～10份、碳酸镁5～10份、三聚磷酸纳4～6份、十二烷基硫酸钠1～3份、木质素磺酸纳3～5份。2.根据权利要求1所述的一种水泥窑余热发电用耐磨耐高温涂料，其特征在于，由以下重量份的组分组成：硅莫砖粉60份，氟石膏15份，硅灰4份，矿渣4份，铝酸盐水泥15份，高铝细粉10份、氧化铝粉8份、碳酸镁7份、三聚磷酸纳5份、十二烷基硫酸钠2份、木质素磺酸纳4份。3.根据权利要求1所述的一种水泥窑余热发电用耐磨耐高温涂...
【专利技术属性】
技术研发人员：吴树全，
申请(专利权)人：徐州苏牌高温新材料有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。